The density of three kinds of molten slags was measured by modified sessile drop method at 1 803-1 873 K. The density of molten slag is found to decrease with increasing temperature. The temperature coefficients of Na2O-Li2O-SiO2 and Li2O-SiO2-B2O3 slag are smaller than that of Na2O-B2O3 slag. The molar volume of slags increases with increasing temperature.
|||Mukai K;Sakao H;Sano K .The Surface Tension and theDensity of MnO-SiO2-Al2O3 Slags at 1 570 ℃[J].Journal of the Japan Institute of Metals,1967,31(08):928-933.|
|||Hara S;Ogino K .Densities and Surface Tension of Melts inthe System CaF2-CaO-SiO2[J].Tetsu To Hagane-Journal of The Iron and Steel Institute of Japan,1989,75(03):439-445.|
|||Yu Z;Mukai K .Measurement of Surface Tension and Densityof Liquid Oxides from Meniscus Shape[J].Journal of the Japan Institute of Metals,1995,59(08):806-813.|
|||Kusuhiro Mukai;Feng Xiao .Density of Ni-Cr alloy in liquid and solid-liquid coexistence states[J].Materials transactions,2002(5):1153-1160.|
|||XIAO Feng,MUKAI Kusuhiro.Study of Interfacial Tension between Molten Steel and Na2O-Li2O-SiO2-B2O3 Slag[J].钢铁研究学报(英文版),2002(01):6-11.|
|||Steinberg D J .A Simple Relationship between the TemperatureDependence of the Density of Liquid Metals and Their BoilingTemperatures[J].Metallurgical and Materials Transactions,1974,5(08):1341-1343.|