中国有色金属学报(英文版), 2017, 27(2): 241-249.
10.1016/S1003-6326(17)60028-1
Al?Cu?Li合金AA2195在低应变速率和3.5%NaCl溶液中的抗裂性能

R.GHOSH 1, , A.VENUGOPAL 2, , P.RAMESHNARAYANAN 3, , S.C.SHARMA 4, , P.V.VENKITAKRISHNAN 5,

1.Materials and Metallurgy Group, Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Thiruvananthapuram-695022, Kerala, India;
2.Materials and Metallurgy Group, Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Thiruvananthapuram-695022, Kerala, India;
3.Materials and Metallurgy Group, Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Thiruvananthapuram-695022, Kerala, India;
4.Materials and Metallurgy Group, Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Thiruvananthapuram-695022, Kerala, India;
5.Materials and Metallurgy Group, Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Thiruvananthapuram-695022, Kerala, India
研究Al?Cu?Li合金AA2195在3.5%NaCl环境中的耐蚀和抗裂性能,并将其与另一高强合金AA2219进行比较.采用浸泡腐蚀和恒电位极化实验测定合金的总耐蚀性能;采用低应变速率测试法确定合金的应力腐蚀开裂(SCC)性能.利用SEM?EDS和光学测量技术对合金样品进行表征以研究其腐蚀形貌、元素含量和腐蚀深度的变化.用韧性的减少量作为估算合金应力腐蚀开裂(SCC)敏感性的一个参数.结果表明,由于较低的腐蚀速率、较小的腐蚀深度和宽度,AA2195合金比AA2219合金具有更好的耐蚀性能.然而,两种合金的SCC参数(εNaCl/εair)均大于0.90,说明此两种合金均具有较好的抗裂性能.断裂样品的SEM?EDS结果表明,两种合金均为典型的脆性断裂形貌.
引用： R.GHOSH, A.VENUGOPAL, P.RAMESHNARAYANAN, S.C.SHARMA, P.V.VENKITAKRISHNAN Al?Cu?Li合金AA2195在低应变速率和3.5%NaCl溶液中的抗裂性能. 中国有色金属学报(英文版), 2017, 27(2): 241-249. doi: 10.1016/S1003-6326(17)60028-1