中国有色金属学报(英文版), 2017, 27(3): 475-492.
10.1016/S1003-6326(17)60055-4
变形温度对6082铝合金析出相、显微组织演变、力学性能和腐蚀行为的影响

Nikhil KUMAR 1, , R.JAYAGANTHAN 2, , Heinz-GünterBROKMEIER 3,

1.Department of Metallurgical and Materials Engineering & Centre of Nanotechnology, Indian Institute of Technology Roorkee, Roorkee 247667, India;
2.Department of Metallurgical and Materials Engineering & Centre of Nanotechnology, Indian Institute of Technology Roorkee, Roorkee 247667, India;Department of Engineering Design, Indian Institute of Technology Madras, Chennai 600036, India;
3.Institute of Materials Science and Engineering, Clausthal University of Technology, Agricolastrasse 6, D-38678 Clausthal-Zellerfeld, Germany & Helmholtz Zentrum Geesthacht, Max Planck Stra?e 1, D-21502 Geesthacht, Germany
研究深冷轧制、室温轧制和后续退火对6082铝合金析出相、显微组织演变(回复,再结晶与晶粒生长)、力学性能和腐蚀行为的影响.采用差示扫描量热仪、透射电子显微镜和背散射电子衍射研究深冷轧制、室温轧制及后续热处理样品的析出动力学和显微组织形貌,以探讨其力学性能.经200°C退火后,深冷轧制样品的抗拉强度和硬度(345 MPa和HV 127)比室温轧制样品的抗拉强度和硬度(320 MPa和HV 115)更高.200°C退火后深冷轧制样品抗拉强度和硬度得到提高是因为铝基体中析出β'相,与室温轧制样品相比产生更大的Zener阻力.与室温轧制样品的腐蚀和点蚀电位(?1.335 V和?710 mV)相比,深冷轧制样品的腐蚀和点蚀电位(?1.321 V和?700 mV)也得到提高.深冷轧制样品具有较高的位错密度,Mg 4 Al 3 Si 4析出相溶解到基体中,通过形成钝化保护层和抑制原电池的形成,使样品的抗腐蚀性能得到提高.