A New Method to Quickly Assess the Inhibitor Efficiency

武汉理工大学学报-材料科学版(英文版), 2008, 23(6): 950-954. doi: 10.1007/s11595-007-6950-9

^1, , ^2, , ^3,

1.Key Laboratory of Advanced Materials,Department of Materials Science and Engineering,Tsinghua University,Beijing 100084,China

2.Key Laboratory of Advanced Materials,Department of Materials Science and Engineering,Tsinghua University,Beijing 100084,China

3.Key Laboratory of Advanced Materials,Department of Materials Science and Engineering,Tsinghua University,Beijing 100084,China

A New Method to Quickly Assess the Inhibitor Efficiency

GENG Chunlei ^1, , XU Yongmo ^2, , WENG Duan ^3,

1.Key Laboratory of Advanced Materials,Department of Materials Science and Engineering,Tsinghua University,Beijing 100084,China

2.Key Laboratory of Advanced Materials,Department of Materials Science and Engineering,Tsinghua University,Beijing 100084,China

3.Key Laboratory of Advanced Materials,Department of Materials Science and Engineering,Tsinghua University,Beijing 100084,China

Keywords： inhibitors

A new method to quickly assess the efficiency of corrosion inhibitor was developed by electrically accelerating chloride ions diffusing onto the surface of the embedded steel bar in concrete and inducing corrosion.Potentiodynamic polarization scanning and linear polarization method were used to evaluate the corrosion states which were compared with the direct observation of the bar surface by breaking the sample.The test duration was about two days and the results clearly show the differences in efficiency of the inhibitors tested.

参考文献

[1]	Hong D H.Corrosion and Protection of Steel Bar in Concrete[M].北京:中国铁道出版社,1998:1-184.
[2]	Saraswathya V;Song H W .Improving the Durability of Concrete by Using Inhihitors[J].Building and Environment,2007,42:464-472.
[3]	Ormellese M;Berra M;Bolzoni F et al.Corrosion lnhibitors for Chlorides Induced Corrosion in Reinforced Concrete Structures[J].Cement and Concrete Research,2006,36:536-547.
[4]	Neal S. Berke;Maria C. Hicks .Predicting long-term durability of steel reinforced concrete with calcium nitrite corrosion inhibitor[J].Cement & concrete composites,2004(3):191-198.
[5]	Fedrizzia L;Azzolinib F;Bonora P L .The Use of Migrating Corrosion lnhibitors to Repair Motorways' Concrete Structures Contaminated by Chlorides[J].Cement and Concrete Research,2006,35:551-561.
[6]	Malik.A U;Andijani I;Al-Moaili F et al.Studies on the Performance of Migratory Corrosion lnhibitors in Protection of Rebar Concrete in Gulf Seawater Environment[J].Cement and Concrete Composites,2004,26:235-242.
[7]	徐永模.迁移性阻锈剂--钢筋混凝土阻锈剂的新发展[J].硅酸盐学报,2002(01):94-101.
[8]	Li G;Liu T;Fei J X.Accelerated Effects of Rebar's Corrosion Rate Inconcrete under the Wet Dry Cycling Condition[J].Concrete,2005(10):108-111.
[9]	姬永生,袁迎曙.干湿循环作用下氯离子在混凝土中的侵蚀过程分析[J].工业建筑,2006(12):16-19,23.
[10]	Rob B. Polder;Willy H.A. Peelen .Characterisation of chloride transport and reinforcement corrosion in concrete under cyclic wetting and drying by electrical resistivity[J].Cement & concrete composites,2002(5):427-435.
[11]	GB 8076-1997.GB 8076-1997.Standard of the People's Republic of China:Concrete admixtures[S].
[12]	Tang L P;Nilsson L O .Rapid Determination of the Chloride Diffusivity in Concrete by Applying an Electrical Field[J].ACI Materials Journal,1992,89(01):49-53.
[13]	NordTest NT Build 492.NordTest NT Build 492.Chloride Diffusion Coefficient From Non-Steady-State Diffusion Experiments[S].Nordtest,Tekniikantie Espoo,Finland,1999.
[14]	李美利,钱觉时,王丽娟,楚爱群,叶宁,杨展.高性能混凝土的养护[J].河南科学,2006(01):107-110.
[15]	C 1202-1994.C 1202-1994.Standard Test Method for Electrical Indication of Concrete's Ability to Resist Chloride Ion Penetration[S].West Conshohocken,PA,1994.
[16]	Jones M R;Dhir R K;Gill J P .Concrete Surface Treatment:Effect of Exposure Temperature on Chloride Diffusion Resistance[J].Cement and Concrete Research,1995,25:197-208.
[17]	王仁超,朱琳,李振富.混凝土氯离子综合机制扩散模型及敏感性研究[J].哈尔滨工业大学学报,2004(06):824-828.
[18]	耿欧,李果,袁迎曙.电化学检测技术在混凝土内钢筋腐蚀研究中的应用现状与展望[J].混凝土,2005(02):20-23.
[19]	朱敏,何积铨,李成华,郑秋麟,任新广.IR降对混凝土中钢筋腐蚀电化学测量结果的影响[J].北京科技大学学报,2002(02):111-114.
[20]	Song G I .Theoretical Analysis of the Measurement of Polarisation Resistance lnreinforced Concrete[J].Cement and Concrete Composites,2000,22:407-415.
[21]	G 5-1994.G 5-1994.Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements[S].West Conshohocken,PA,1994.
[22]	G 59-1991.G 59-1991.Test Method for Conducting Potentiodynamic Polarization Resistance Measurements[S].West Conshohocken,PA,1991.
[23]	Millard S G;Law D;Bungey J H .Environmental Influences on Linear Polarisation Corrosion Rate Mesasurement in Reinforced Concrete[J].NDT & E International,2001,34:409-417.
[24]	田冠飞,安雪晖.钢筋存在对氯离子扩散阻滞影响的有限元分析[J].混凝土,2006(05):1-3,6.
[25]	Stanley C.Kranc;Alberto A.Sagues;Francisco J.Presuel-Moreno .Decreased corrosion initiation time of steel in concrete due to reinforcing bar obstruction of diffusional flow[J].ACI materials journal,2002(1):51-53.
[26]	Hong N F .Steel Corrosion and Protective Technology in Concrete-rebar Inhibitor Admixture and Cathode Protection[J].Industrial Construction,2000,30(I):57-60.
[27]	Xu Y M;She H L;Boris A Miksic.Comparative Study of Inhibitors MCI and Sodium Nitrite in Carbonation and Chloride Induced Corrosion of Steel in Concrete[J].Materials Performance,2004(01):42-46.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

A New Method to Quickly Assess the Inhibitor Efficiency

参考文献