Using carbide slag as the calcareous materials, xonotlite thermal insulation material was successfully prepared via dynamic hydrothermal synthesis. The experimental results show that the xonotlite thermal insulation material is made up of large numbers of "chestnut bur shape" particles. Optimum conditions of calcination temperature of carbide slag, synthesis reaction temperature and time, stirring rate, CaO/SiO2 mol ratio, water/solid weight ratio, amount of fiberglass, molding pressures, dryness temperatures and the presence of dispersant (glycol and polyvinyl alcohol) favor the preparation of xonotlite thermal insulation material. The evaluation of xonotlite thermal insulation material reveals that the product is ultra-light and excellent in physical performances. Such a little amount of impurities in carbide slag has no effect on the phase, morphology, stability at high temperature and physical performances of products.
参考文献
| [1] | 李懋强.水热合成硅酸钙微孔球形颗粒[J].硅酸盐学报,2002(z1):64-67. |
| [2] | 梁宏勋,李懋强.硬硅钙石水热合成的形成历程及硝酸锶对它的影响[J].硅酸盐学报,2002(03):294-299. |
| [3] | N. B. Milestone;K. Ghanbari Ahari .Hydrothermal processing of xonotlite based compositions[J].Advances in Applied Ceramics,2007(6):302-308. |
| [4] | Udawatte C.P.;Yanagisawa K. .Solidification of xonotlite fibers with chitosan by hydrothermal hot pressing[J].Materials Letters,2000(6):298-301. |
| [5] | 高积强,黄清伟,仵亚红,殷晓东,金志浩.流延法制备短纤维增强玻璃陶瓷基复合材料[J].复合材料学报,1999(02):105-109. |
| [6] | 曾令可,曹建新,王慧,刘平安.硬硅钙石--SiO2复合纳米孔超级绝热材料[J].陶瓷学报,2004(02):75-80. |
| [7] | 肖晋宜,倪文,王坤英,陈德平,刘凤梅.搅拌对动态水热合成硬硅钙石二次粒子形貌的影响[J].非金属矿,2007(04):31-33,49. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%