Effects of Al2O3 and Ni as the additives on the sinterability,microstructure and mechanical properties were systematic studied.The experimental results show that only a relative density about 96.2% of hot-pressing TiB2-30%Al2O3 can be attained due to the plate-like TiB2 particle and its random orientation and excessive Al2O3 grain growth.When sintering temperature is higher than 1700 ℃,TiB2 grain growth can be found,which obvious improves flexural strength of TiB2 matrix but decreases toughness.It seems that mechanical properties of TiB2-Al2O3 composites are mainly depended on relative density besides grain growth.otherwise,they will be determined by relative density and TiB2 matrix strength together.Anyway,Al2O3 addition can weaken the grain boundary and thus improve the toughness of the materials.A flexural strength of 529 MPa,Al2O3.
参考文献
| [1] | Andreas Krell;Paul Blank;Hongwei Ma .Processing of High-Density Submicrometer Al_2O_3 for New Applications[J].Journal of the American Ceramic Society,2003(4):546-553. |
| [2] | Tang WJ;Fu ZY;Zhang JY;Wang W;Wang H;Wang YC;Zhang QJ .Fabrication and characteristics of TiB2/Al2O3 core/shell particles by hybridization[J].Powder Technology: An International Journal on the Science and Technology of Wet and Dry Particulate Systems,2006(3):117-123. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%