Butt joints between Mg alloy AZ31B and pure Al 1 060 sheets were produced via metal inert gas welding process with Zn-Cd alloy foil. Crack-free Al/Mg butt joints between AZ31B Mg alloy and pure Al 1060 sheets were obtained. Intermetallic compound layer 1 and layer 2 had formed in fusion zone/Mg alloy and the average thickness of the layer 1 was about 50μm. The intermetallic compound layer 1 consisted of Al12Mg17 and Mg2Si phases while layer 2 consisted of Al12Mg17, Mg2Si and MgZn2 phases. The crack started from the IMC layer at the bottom of the joint and propagated along the brittle IMC layer, then expanded into weld metal during the SEM in situ tensile test. The highest tensile strength of the dissimilar metal butt joints could reach 46.8 MPa and the effect of interfacial IMC layer on mechanical property of the joint was discussed in detail in the present study.
参考文献
| [1] | WANG Hongxia,LIANG Wei,XUE Jinbo,ZHAO Xingguo,BIAN Liping,ZHANG Jinshan.Microstructure and Mechanical Properties of Ultrafine Grained Mg15Al Alloy Processed by Equal-channel Angular Pressing[J].武汉理工大学学报（材料科学版）（英文版）,2010(02):238-242. |
| [2] | ZHANG Zhiqiang,LE Qichi,CUI Jianzhong.Microstructure Evolution of AS41 Magnesium Alloy Fabricated by Ultrasonic Vibration[J].武汉理工大学学报（材料科学版）（英文版）,2010(05):820-823. |
| [3] | H.T. Zhang;X.Y. Dai;J.C. Feng .Joining of aluminum and magnesium via pre-roll-assisted A-TIG welding with Zn interlayer[J].Materials Letters,2014(May.1):49-51. |
| [4] | Zhi Wang;Hongyang Wang;Liming Liu .Study on low temperature brazing of magnesium alloy to aluminum alloy using Sn-xZn solders[J].Materials & design,2012(Aug.):14-19. |
| [5] | A.C. Somasekharan;L.E. Murr .Microstructures in friction-stir welded dissimilar magnesium alloys and magnesium alloys to 6061-T6 aluminum alloy[J].Materials Characterization,2004(1):49-64. |
| [6] | Venkateswaran, P.;Reynolds, A.P..Factors affecting the properties of Friction Stir Welds between aluminum and magnesium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:26-37. |
| [7] | Lin DC.;Wang GX.;Srivatsan TS. .A mechanism for the formation of equiaxed grains in welds of aluminum-lithium alloy 2090[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):304-309. |
| [8] | WANG Ping,MEI Bingchu,HONG Xiaolin,ZHU Jiaoqun,ZHOU Weibing.Fabrication of Ti2AlC by Spark Plasma Sintering from Elemental Powders and Thermodynamics Analysis of Ti-Al-C System[J].武汉理工大学学报（材料科学版）（英文版）,2007(02):325-328. |
| [9] | B. Straumal;R. Valiev;O. Kogtenkova .Thermal evolution and grain boundary phase transformations in severely deformed nanograined Al-Zn alloys[J].Acta materialia,2008(20):6123-6131. |
| [10] | Fei Liu;Zhaodong Zhang;Liming Liu.Microstructure evolution of Al/Mg butt joints welded by gas tungsten arc with Zn filler metal[J].Materials Characterization,2012:84-89. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%