The aim of this study was to improve the cyclic oxidation resistance of In718 superalloy by laser peening(LP). Specimens were treated by LP from one to three times, respectively. The cyclic oxidation tests at 900℃ for periods up to 2 h were conducted. Changes of the top surface morphology and microstructure were analyzed by scanning electron microscope (SEM), energy-dispersive spectra (EDS), transmission electron microscope (TEM) and X-ray diffraction technique (XRD), respectively. The weights were measured between the oxidation cycles to assess the oxidation of the specimens. The top surface microstructure after LP was characterized by highly tangled and dense dislocation arrangements and a high amount of twins. Protective oxidation layer was generated more quickly on the surface treated by LP. The average oxidation rate was about 50 % lower. A tiny homogeneous oxidation layer containing (Fe,Cr)2O3, NiCrO3 and Ni(Al,Cr)2O4 spinel was generated on the surface. The experimental results of cyclic oxidation tests show that specimens treated by LP have a better high temperature oxidation resistance, and the antistrip performance of the oxidation layer improves. Moreover, the effects of LP are strengthened with the increase of laser peening.
参考文献
| [1] | Morales M;Porro JA;Blasco M et al.Numerical Simulation of Plasma Dynamics in Laser Peening Experiments[J].Applied Surface Sinence,2009,255:5181-5182. |
| [2] | Tong X;Dai MJ;Zhang ZH .Thermal Fatigue Resistance of H13 Steel Treated by Selective Laser Surface Melting and CrNi Alloying[J].Applied Surface Sinence,2013,01(209):373-380. |
| [3] | Rouleau B;Peyre P;Breuils J et al.Characterization at A Local Scale of A Laser-shock Peened Aluminum Alloy Surface[J].Applied Surface Sinence,2011,257:7195-7203. |
| [4] | Altenberger I;Nalla RK;Sano YJ et al.On the Effect of Deep-rolling and Laser-peening on the Stress-controlled Low-and High-Cycle Fatigue Behavior of Ti-6Al-4V at Elevated Temperatures up to 550℃[J].International Journal of Fatigue,2012,44:292-302. |
| [5] | Cao ZW;Xu HY;Zou SK et al.Investigation of Surface Integrity on TC17 Titanium Alloy Treated[J].Chinese J Aeronaut,2012,25:650-656. |
| [6] | Uro?T;Janez G .Evaluation of Corrosion Resistance of AA6082-T651 Aluminium Alloy after Laser Shock Peening by Means of Cyclic Polarisation and ElS Methods[J].Corrosion Science,2012,59:324-333. |
| [7] | Zhang L;Zhang YK;Lu JZ et al.Effects of Laser Peening on Electrochemical Corrosion Resistance of ANSI 304 Stainless Steel Weldments after Cavitation Erosion[J].Corrosion Science,2013,66:5-13. |
| [8] | Amar H;Vignal V;Krawiec H et al.Inlfuence of the Microstructure and Laser Peening(LP)on the Corrosion Behaviour of the AA2050-T8 Aluminium Alloy[J].Corrosion Science,2011,53:3215-3220. |
| [9] | Zhang L;Lu JZ;Zhang YK et al.Effects of Different Shocked Paths on Fatigue Property of 7050-T7451 Aluminum Alloy during Two-sided Laser Peening[J].Materials and Design,2011,32:480-486. |
| [10] | Lu JZ;Luo KY;Yang DK et al.Effects of Laser Peening on Stress Corrosion Cracking(SCC)of ANSI 304 Austenitic Stainless Steel[J].Corrosion Science,2012,60:145-152. |
| [11] | Loria E A .The Status and Prospects of Alloy 718[J].JOURNAL OF METALS,1988,7:36-41. |
| [12] | Greene GA;Finfrock CC .Oxidation of Inconel 718 in Air at High Temperatures[J].Oxidation of Metals,2001,55:505-521. |
| [13] | Zhou CH;Zhang ZY;Zhang QM .Comparison of the Hot Corrosion of Nanostructured and Microstructured Thermal Barrier Coatings[J].Materials and Corrosion,2012,63:613-618. |
| [14] | Rubio-González C;Gomez-Rosas G;Ocana JL et al.Effect of An Absorbent Overlay on the Residual Stress Field Induced by Laser Peening on Aluminum Samples[J].Applied Surface Sinence,2006,252:6201-6205. |
| [15] | Li ZM;Qian SQ;Wang W et al.Microstructure and Oxidation Resistance of Magnetron-sputtered Nano Crystalline NiCoCrAlY Coatings on Nickel-based Superalloy[J].Journal of Alloys and Compounds,2010,505:675-679. |
| [16] | Li Liu;Ying Li;Fuhui Wang .The effect of micro-structure on the oxidation behavior of a Ni-based superalloy in water vapor plus oxygen[J].Materials Letters,2008(25):4081-4084. |
| [17] | Giggins CS;Pettit FS .Oxidation of Ni-Cr alloys between 800° and 1 200℃[J].TAIME,1969,4:1088-1097. |
| [18] | Birks N;Rickert H .Oxidation Mechanism of Some Nickel-chromium Alloys[J].Inst J Met,1962,63(91):308-315. |
| [19] | Wood GC .The Morphology and Mechanism of Formation of Porous Anodic Films on Aluminium[J].Oxidation of Metals,1970,2:11-15. |
| [20] | Wood GC;Wright IG;Hodgkiess T .A Comparison of the Oxidation of Fe[J].Werkst Korr,1970,21:900-910. |
| [21] | Wood GC;Chattopadhyay B .The Transient Oxidation of Alloys[J].Corrosion Science,1970,2:373-379. |
| [22] | He J;Guo HB;Peng H et al.Microstructural,Mechanical and Oxidation Features of NiCoCrAlY Coating Produced by Plasma Activated EB-PVD[J].Applied Surface Sinence,2013,274:144-150. |
| [23] | Wei DB;Zhang PZ;Yao Z et al.Cyclic Oxidation Behavior of Plasma Surface Chromising Coating on Titanium Alloy Ti-6Al-4V[J].Applied Surface Sinence,2012,261:800-806. |
| [24] | Graham MJ;Hussey RJ .Analytical Techniques in High Temperature Corrosion[J].Oxidation of Metals,1995,44:339-374. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%