Hot deformation behaviors were studied by means of scanning electron microscopy (SEM) and uniaxial thermal tension. The effect of de-formation temperature and strain rate on flow stress was evaluated, and deformation mechanism was analyzed. The results show that the stress-strain curves of Ti-6Al-4V (TC4) alloy sheet and TC4 alloy bar at elevated temperatures have different forms and rules. Flow stress of TCA is controlled by both strain rate and deformation temperature. The flow stress decreases with the increase of high temperature. Deforma-tion mechanisms exhibit dynamic recovery and recrystallization feature within high temperature region and grain boundary slip behaviors at low temperature.
参考文献
| [1] | Liu Y;Zhu J C;Wang Y;Zhan J J .Hot compressive deformation behaviors and micro-mechanisms of TA15 alloy[J].RARE METALS,2007,27(z1):162. |
| [2] | A.B. Li;L.J. Huang;Q.Y. Meng;L. Geng;X.P. Cui .Hot Working Of Ti-6al-3mo-2zr-0.3si Alloy With Lamellar α +βstarting Structure Using Processing Map[J].Materials & design,2009(5):1625-1631. |
| [3] | Luo, J;Li, MQ;Li, H;Yu, WX .Effect of the strain on the deformation behavior of isothermally compressed Ti-6Al-4V alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2009(1/2):88-95. |
| [4] | Fang X Y;Yi D Q;Wang B;Wu C P,and Zhang H .Hot compression deformation behavior of the Mg-Al-Y-Zn magnesium alloy[J].Rare Metals,2008,27(02):121. |
| [5] | T. Seshacharyulu;Steve C. Medeiros;William G. Frazier .Unstable flow during supratransus working of Ti-6Al-4V[J].Materials Letters,2001(3):133-139. |
| [6] | DUAN Yuan-pei,LI Ping,XUE Ke-min,ZHANG Qing,WANG Xiao-xi.Flow behavior and microstructure evolution of TB8 alloy during hot deformation process[J].中国有色金属学会会刊（英文版）,2007(06):1199-1204. |
| [7] | O. A. Kaibyshev .Grain refinement in commercial alloys due to high plastic deformations and phase transformations[J].Journal of Materials Processing Technology,2001(3):300-306. |
| [8] | Seshacharyulu T.;Medeiros SC.;Frazier WG.;Prasad YVRK. .Microstructural mechanisms during hot working of commercial grade Ti-6Al-4V with lamellar starting structure[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):112-125. |