A series of Eu2+-doped ternary nitride phosphors, with a formula of (Sr1-xCax)2Si5N8: Eu2+, were synthesized by high-temperature solid-state method. The structure and luminescence properties were characterized, indicating the potential application as a red phosphor in the phosphor-converted white light-emitting diodes. The X-ray diffraction patterns showed that the Sr2Si5N8 and Ca2Si5N8 phases were generated at each end of (Sr1-xCax)2Si5N8: Eu2+ and coexisted in the range of 0.5≤x≤0.75. The emission spectra showed broad emission bands originating from the 4f65d1→4f7 transition of Eu2+ ions. The emission peak changed with the variations in Ca2+ concentration.
参考文献
[1] | Nakamura S;Mukai T;Senoh M .Candela-class-high brightness InGaN/A1GaN double-heterrostructure blue LEDs[J].Applied Physics Letters,1994,64:1687. |
[2] | 苏锵,吴昊,潘跃晓,徐剑,郭崇峰,张新民,张剑辉,王静,张梅.稀土发光材料在固体白光LED照明中的应用[J].中国稀土学报,2005(05):513-517. |
[3] | Piao Xianqing;Horikaw T;Hanzawa H;Machida K .Photoluminescence properties of Ca2Si5N8:Eu2+ nitride phosphor prepared by carbothermal reduction and nitridation method[J].Chemistry Letters,2006,35(23):334. |
[4] | Li Y Q;van Steen J E J;van Krevel J W H;Botty G Delsing A C A Disalvo F J With G de Hintzen H T .Luminescence properties of red-emitting M2Si5N8:Eu2+ (M=Ca,Sr,Ba) LED conversion phosphors[J].Journal of Alloys and Compounds,2006,417:273. |
[5] | Schlotter P;Baur J;Hielscher Ch;Kunzer M Obloh H Schmidt R Schneider J .Fabrication and characterization of GaN/InGaN/AlGaN double heterostructure LEDs and their application in luminescence conversion LEDs[J].Materials Science and Engineering B:Solid State Materials for Advanced Technology,1999,59:390. |
[6] | Nakamura S;Fasol G.The Blue Laser Diodes,GaN Based Light Emitters and Laser[M].Berlin:Spirnger,1997:216. |
[7] | 李东平,缪春燕,刘丽芳,夏威.白光LED用YAG∶Ce3+荧光粉的研究进展[J].液晶与显示,2005(06):526-531. |
[8] | Yuexiao Pan;Mingmei Wu;Qiang Su .Comparative investigation on synthesis and photoluminescence of YAG:Ce phosphor[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2004(3):251-256. |
[9] | 张书生,庄卫东,赵春雷,胡运生,何华强,黄小卫.Study on(Y,Gd)3(Al,Ga)5O12∶Ce3+ Phosphor[J].稀土学报(英文版),2004(01):118-121. |
[10] | Bogner G;Botty G;Braune B;Hintzen H T,van Krevel J W H,Waitl G .Light source using a yellow-to-red-emitting phosphor[P].United States Patent:US 2003/0020101 A1,2003-1-30. |
[11] | Li Jinwang;Tomoaki W;Hiroshi W;Tohru S Masahiro Y .Low-temperature crystallization of Eu-doped red-emitting CaAlSiN3 from alloy-derived ammonometallates[J].Chemistry of Materials,2007,19:3592. |
[12] | Hoppe HA.;Morys P.;Schnick W.;Seilmeier A.;Lutz H. .Luminescence in Eu2+-doped Ba2Si5N8: fluorescence, thermoluminescence, and upconversion[J].The journal of physics and chemistry of solids,2000(12):2001-2006. |
[13] | Xie RJ;Hirosaki N;Suehiro T;Xu FF;Mitomo M .A simple, efficient synthetic route to Sr2Si5N8 : Eu2+-based red phosphors for white light-emitting diodes[J].Chemistry of Materials: A Publication of the American Chemistry Society,2006(23):5578-5583. |
[14] | Piao Xianqing;Horikawa T;Hanzawa H;Machida K .Characterization and luminescence properties of Sr2Si5N8:Eu2+ phosphor for white light-emitting-diode illumination[J].Applied Physics Letters,2006,88:161908. |
[15] | Piao Xianqing;Machida K;Horikawa T;Hanzawa H .Self-propagating high temperature synthesis of yellow-emitting Ba2Si5N8:Eu2+ phosphors for white light-emitting diodes[J].Applied Physics Letters,2007,91:041908. |
[16] | TENG Xiaoming,ZHUANG Weidong,HU Yunsheng,HUANG Xiaowei.Luminescence properties of nitride red phosphor for LED[J].稀土学报(英文版),2008(05):652-655. |
[17] | Blasse G;Grabmaier B C.Luminescent Materials[M].Beilin:Springer-Verlag,1994 |
[18] | Blasse G.Luminescence of Inorganic Solids[M].New York:Plenum Press,1978 |
[19] | Hirosaki N;Xie R J;Kimoto K;Sekiguchi T Yamamoto Y Suehiro T Mitomo M .Characterization and properties of green-emitting β-SiAlON:Eu2+ powder phosphors for white light-emitting diodes[J].Applied Physics Letters,2005,86:211905. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%