A complex film on hot-dip galvanized steel sheet (HDG) was prepared by immersing the sheet in 0.1wt.% Ce(NO3)3 solution and 5vol.% silane solution in turn. The corrosion protection of the complex film was evaluated by potentiodynamic linear polarization(LPR), electrochemical impendence spectra (EIS) and natural salt spray (NSS) tests and compared with that of single cerium film and silane film. The results showed that, the presence of these films on the zinc coating hindered corrosion reaction by reducing the rate of both anodic and cathodic reaction in the corrosion process, and the corrosion protection of the complex film was much better than that of single cerium film or silane film and closed to that of chromate film, because the polarization resistance Rp and electrochemical impendence were increased markedly. Microstructure and chemical composition of these pretreated films were also investigated by scanning electron microscopy (SEM) and AES.
参考文献
| [1] | Eichinger E;Osborne J;Cleave T V .Hexavalent chromium elimination:an aerospace industry progress report[J].Metal Finishing,1997,95(03):36. |
| [2] | Almeida E.;Figueiredo MO.;Sa C.;Diamantino TC. .Oxidising alternative species to chromium VI in zinc galvanised steel surface treatment. Part 1 - A morphological and chemical study[J].Surface & Coatings Technology,1998(1):8-17. |
| [3] | 卢锦堂,孔纲,陈锦虹,许乔瑜,眭润舟.Growth and corrosion behavior of molybdate passivation film on hot dip galvanized steel[J].中国有色金属学会会刊(英文版),2003(01):145-148. |
| [4] | Veeraraghavan B.;Slavkov D.;Prabhu S.;Nicholson M.;Haran B.;Popov B. Heimann B. .Synthesis and characterization of a novel non-chrome electrolytic surface treatment process to protect zinc coatings[J].Surface & Coatings Technology,2003(1):41-51. |
| [5] | Hinton B R W;Wilson L .The corrosion inhibition of zinc with cerous chloride[J].Corrosion Science,1989,29(09):967. |
| [6] | Kunitsugu Aramaki .The inhibition effects of cation inhibitors on corrosion of zinc in aerated 0.5 M NaCl[J].Corrosion Science,2001(8):1573-1588. |
| [7] | Aramaki K .Treatment of zinc surface with cerium (Ⅲ) nitrate to prevent zinc corrosion in aerated 0.5 M NaCl solution[J].Corrosion Science,2001,43(11):2201. |
| [8] | Aramaki K .A self-healing protective film prepared on zinc by treatment in a Ce(NO3)3 solution and modification with Ce(NO3)3[J].Corrosion Science,2005,47(05):1285. |
| [9] | LU Jin-tang,WU Hai-jiang,KONG Gang,CHE Chun-shan,XU Qiao-yu.Growth and corrosion behavior of rare earth film on hot-dip galvanized steel[J].中国有色金属学会会刊（英文版）,2006(06):1397-1401. |
| [10] | Manov S;Lamazouere A M;Aries L .Electrochemical study of the corrosion behaviour of zinc treated with a new organic chelating inhibitor[J].Corrosion Science,2000,42(07):1235. |
| [11] | Aramaki K .Effects of organic inhibitors on corrosion of zinc in an aerated 0.5M NaCl solution[J].Corrosion Science,2001,43(10):1985. |
| [12] | Yuan W;van Ooij W J .Characterization of organofunctional silane films on zinc substrates[J].Journal of Colloid and Interface Science,1997,185(01):197. |
| [13] | Zhu DQ.;van Ooij WJ. .Corrosion protection of metals by water-based silane mixtures of bis-[trimethoxysilylpropyl]amine and vinyltriacetoxysilane [Review][J].Progress in Organic Coatings: An International Review Journal,2004(1):42-53. |
| [14] | Danqing Zhu;Wim J. van Ooij .Enhanced corrosion resistance of AA 2024-T3 and hot-dip galvanized steel using a mixture of bis-[triethoxysilylpropyl]tetrasulfide and bis-[trimethoxysilylpropyl]amine[J].Electrochimica Acta,2004(7):1113-1125. |
| [15] | Graeve I;Vereecken J;Franquet A;Van Schaftinghen T;Terryn H .Silane coating of metal substrates: Complementary use of electrochemical, optical and thermal analysis for the evaluation of film properties[J].Progress in Organic Coatings: An International Review Journal,2007(3):224-229. |
| [16] | Trabelsi W;Cecilio P;Ferreira MGS;Montemor MF .Electrochemical assessment of the self-healing properties of Ce-doped silane solutions for the pre-treatment of galvanised steel substrates[J].Progress in Organic Coatings: An International Review Journal,2005(4):276-284. |
| [17] | Trabelsi W;Cecilio P;Ferreira MGS;Yasakau K;Zheludkevich ML;Montemor MF .Surface evaluation and electrochemical behaviour of doped silane pre-treatments on galvanised steel substrates[J].Progress in Organic Coatings: An International Review Journal,2007(3):214-223. |
| [18] | Montemor M F;Ferreira M G S .Ceriumsalt activated nanoparticles as fillers for silane films:Evaluation of the corrosion inhibition performance on galvanised steel substrates[J].Electrochimica Acta,2007,52:6976. |
| [19] | Dabala M.;Buchberger A.;Calliari I.;Armelao L. .Cerium-based conversion layers on aluminum alloys[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2001(3/4):312-322. |
| [20] | Montemor M F;Simes A M;Ferreira M G S .Composition and behavior of cerium films on galvanised steel[J].Progress in Organic Coatings,2001,43(04):281. |
| [21] | Child T;Van Ooij W J .Application of silane technology to prevent corrosion of metals and improve paint adhesion[J].Transactions of the Institute of Metal Finishing,1999,77(02):64. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%