The La-Co substituted Sr1–xLaxFe12–xCoxO19 (x=0–0.5) ferrites with appropriate Bi2O3 additive were prepared by conventional sintering method and microwave sintering method at low sintering temperatures compatible with LTCC (low temperature co-fired ceramics) systems, and their sintering behavior was chiefly investigated, including the crystal structure, saturation magnetizationMs, magnetic anisotropy fieldHa, intrinsic coercivityHci, and Curie temperatureTC. Experiment results clearly showed that the pure M-type crystal phase was successfully obtained when the La-Co substitution amountx did not exceed 0.3. However, the single M-type phase structure transformed to multiphase structure with further increased x, where the M-type phase coexisted with the non-magnetic phase such asα-Fe2O3 phase, La2O3 phase, and LaCoO3 phase. Appropriate La-Co substitution improved theMs (>62 emu/g),Ha (>1400 kA/m), andHci (>320 kA/m) for the ferrites withx varying from 0.1 to 0.3, but theTC decreased with increasing substitution amount. More-over, the microwave sintered ferrites could provide largerHci and similarMs compared with the conventional sintered ferrites.
参考文献
| [1] | Jensen, T.,Krozer, V.,Kjaergaard, C..Realisation of microstrip junction circulator using LTCC technology[J].Electronics Letters,20112(2):111-113. |
| [2] | 黄新友;邢仁克;高春华;陈志刚.Influence of CeO2 doping amount on property of BCTZ lead-free piezoelectric ceramics sintered at low temperature[J].稀土学报（英文版）,2014(8):733-737. |
| [3] | 吉成;冀立宇;连刘超;沈丽明;张晓艳;王一峰;Arunava Gupta.Low-temperature solution synthesis and characterization of Ce-doped YAG nanoparticles[J].稀土学报（英文版）,2015(6):591-598. |
| [4] | PENG Long;HU Yue-Bin;GUO Cheng;LI Le-Zhong;WANG Rui;HU Yun;TU Xiao-Qiang.Preparation and Magnetic Properties of SrFe12O19 Ferrites Suitable for Use in Self-Biased LTCC Circulators[J].中国物理快报（英文版）,2015(1):150-153. |
| [5] | Peng, Long;Li, Lezhong;Wang, Rui;Hu, Yun;Tu, Xiaoqiang.Effect of La-Co substitution on the crystal structure and magnetic properties of hot press sintered Sr1-xLaxFe12-xCoxO19 (x=0-0.5) ferrites for use in LTCC technology[J].Journal of Magnetism and Magnetic Materials,2015:136-139. |
| [6] | Peng, Long;Li, Lezhong;Wang, Rui;Hu, Yun;Tu, Xiaoqiang;Zhong, Xiaoxi.Effect of La-CO substitution on the crystal structure and magnetic properties of low temperature sintered Sr1-xLaxFe12-xCoxO19 (x=0-0.5) ferrites[J].Journal of Magnetism and Magnetic Materials,2015:399-403. |
| [7] | Liu XS.;Zhong W.;Yang S.;Yu Z.;Gu BX.;Du YW..Influences of La3+ substitution on the structure and magnetic properties of M-type strontium ferrites[J].Journal of Magnetism and Magnetic Materials,20022/3(2/3):207-214. |
| [8] | G. Litsardakis;I. Manolakis;C. Serletis;K.G. Efthimiadis.Effects of Gd substitution on the structural and magnetic properties of strontium hexaferrites[J].Journal of Magnetism and Magnetic Materials,20072(2):170-173. |
| [9] | Liu, XS;Hernandez-Gomez, P;Deng, YX;Huang, K;Xu, XB;Qiu, SX;Zhou, D.Analysis of magnetic disaccommodation in La3+-Co2+-substituted strontium ferrites[J].Journal of Magnetism and Magnetic Materials,200916(16):2421-2424. |
| [10] | Chen, D.;Liu, Y.;Li, Y.;Zhong, W.;Zhang, H..Low-temperature sintering of M-type barium ferrite with BaCu(B _2O_5) additive[J].Journal of Magnetism and Magnetic Materials,20124(4):449-452. |
| [11] | Yuan-xun Li;Ying-li Liu;Huai-wu Zhang;Li-kun Han.The sintering properties and interfacial investigation of barium ferrite and ceramic cofiring system for the application of LTCC technology[J].Journal of Applied Physics,20097(7):07A745-1-07A745-3-0. |
| [12] | Seifert, D;Topfer, J;Langenhorst, F;Le Breton, JM;Chiron, H;Lechevallier, L.Synthesis and magnetic properties of La-substituted M-type Sr hexaferrites[J].Journal of Magnetism and Magnetic Materials,200924(24):4045-4051. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%