通过常温拉伸、晶间腐蚀、慢应变速率应力腐蚀等试验，并结合电子显微观察，研究常规固溶后在不同温度下高温预析出处理对7005铝合金力学性能、腐蚀行为及显微组织的影响。结果表明：合金的维氏硬度随着预析出温度的降低而逐渐下降，而电导率则呈现出相反的变化趋势，并以此选择440和420°C进行预析出对比研究。高温预析出能显著增加晶界粗大析出相的不连续分布程度，且随着预析出温度的降低，晶界析出相的粗化和不连续程度增加，致使合金抗晶间腐蚀和应力腐蚀性能得到显著提高，而强度略有下降。
High temperature pre-precipitation (HTPP)took place in7005 alloy at various temperatures after solution treatment and itsinfluence on mechanical properties, corrosion behaviors and microstructure of the alloy was investigated using tensile test, intergranular corrosion (IGC) test, slow strain rate testing (SSRT), together with microstructural examinations. It is found that Vickers hardness of the aged alloy decreases gradually with decreasing the HTPP temperature, and almost a reverse trend of electrical conductivity is found compared to the hardness changes. Depending on the changes, two HTPP temperaturesof 440 and 420°Cwere chosen for comparative study. Results reveal that HTPP alloy tempers exhibit higher resistance to stress corrosion cracking (SCC) and IGC than none pre-precipitate one with an acceptable strength loss due to the substantial enhancement of distribution discontinuity of the coarse grain boundary precipitates (GBPs), and the coarsening and interspacing effect on GBPs becomes more obvious with decreasing the pre-precipitation temperature.
参考文献
| [1] | A. Heinz;A. Haszler;C. Keidel;S. Moldenhauer;R. Benedictus;W. S. Miller.Recent development in aluminium alloys for aerospace applications[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20001(1):102-107. |
| [2] | LI Jin-feng;PENG Zhuo-wei;LI Chao-xing;JIA Zhi-qiang;CHEN Wen-jing;ZHENG Zi-qiao.Mechanical properties, corrosion behaviors and microstructures of 7075 aluminium alloy with various aging treatments[J].中国有色金属学会会刊（英文版）,2008(04):755-762. |
| [3] | M. Bobby-Kannan;V. S. Raja;R. Raman.Influence of Multistep Aging on the Stress Corrosion Cracking Behavior of Aluminum Alloy 7010[J].Corrosion: The Journal of Science and Engineering,200310(10):881-889. |
| [4] | 陈送义;陈康华;董朋轩;叶升平;黄兰萍.热处理对7085铝合金应力腐蚀开裂、断裂韧性和强度的影响[J].中国有色金属学报（英文版）,2014(7):2320-2325. |
| [5] | 彭国胜;陈康华;陈送义;方华婵.二次回归再时效对Al-Zn-Mg-Cu组织、强度及剥蚀性能的影响[J].中国有色金属学报（英文版）,2012(4):803-809. |
| [6] | S.P. Knight;N. Birbilis;B.C. Muddle;A.R. Trueman;S.P. Lynch.Correlations between intergranular stress corrosion cracking, grain-boundary microchemistry, and grain-boundary electrochemistry for Al-Zn-Mg-Cu alloys[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,201012(12):4073-4080. |
| [7] | Jing-Chie Lin;Hsueh-Lung Liao;Wern-Dare Jehng;Chih-Horng Chang;Sheng-Long Lee.Effect of heat treatments on the tensile strength and SCC-resistance of AA7050 in an alkaline saline solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,200610(10):3139-3156. |
| [8] | BIN-LUNG OU;JI-GANG YANG;MON-YU WEI.Effect of Homogenization and Aging Treatment on Mechanical Properties and Stress-Corrosion Cracking of 7050 Alloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,20078(8):1760-1773. |
| [9] | 陈送义;陈康华;彭国胜;梁信;陈学海.淬火速度对7085铝合金显微组织和应力腐蚀的影响[J].中国有色金属学报（英文版）,2012(1):47-52. |
| [10] | Lanping Huang;Kanghua Chen;Song Li.Influence of grain-boundary pre-precipitation and corrosion characteristics of inter-granular phases on corrosion behaviors of an Al-Zn-Mg-Cu alloy[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,201211(11):862-868. |
| [11] | 黄兰萍;陈康华;李松;刘红卫.高温预析出对Al-Zn-Mg铝合金组织、力学性能和应力腐蚀性能的影响[J].中国有色金属学报,2005(5):727-733. |
| [12] | Shi, Yunjia;Pan, Qinglin;Li, Mengjia;Huang, Xing;Li, Bo.Influence of alloyed Sc and Zr, and heat treatment on microstructures and stress corrosion cracking of Al-Zn-Mg-Cu alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2015:173-181. |
| [13] | T. Ramgopal;P.I. Gouma;G.S. Frankel.Role of Grain-Boundary Precipitates and Solute-Depleted Zone on the lntergranular Corrosion of Aluminum Alloy 7150[J].Corrosion: The Journal of Science and Engineering,20028(8):687-697. |
| [14] | Liu, S. D.;Chen, B.;Li, C. B.;Dai, Y.;Deng, Y. L.;Zhang, X. M..Mechanism of low exfoliation corrosion resistance due to slow quenching in high strength aluminium alloy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2015Feb.(Feb.):203-212. |
| [15] | X.S. Du;Y.J. Su;J.X. Li;L.J. Qiao;W.Y. Chu.Stress corrosion cracking of A537 steel in simulated marine environments[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012Dec.(Dec.):278-287. |
| [16] | 唐建国;陈慧;张新明;刘胜胆;刘文军;欧阳惠;李红萍.淬火析出对Al-Zn-Mg-Cu合金时效行为的影响[J].中国有色金属学报（英文版）,2012(6):1255-1263. |
| [17] | A. H. Moreira;A. V. Benedetti;P. T. A. Sumodjo;J. A. Garrido;P. L. Cabot.Electrochemical behavior of heat-treated Al-Zn-Mg alloys in chloride solutions containing sulphate[J].Electrochimica Acta,200217(17):2823-2831. |
| [18] | Ying Deng;Zhimin Yin;Kai Zhao;Jiaqi Duan;Jian Hu;Zhenbo He.Effects of Sc and Zr microalloying additions and aging time at 120 ℃ on the corrosion behaviour of an Al-Zn-Mg alloy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012Dec.(Dec.):288-298. |
| [19] | Dumont D.;Deschamps A.;Brechet Y..On the relationship between microstructure, strength and toughness in AA7050 aluminum alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20031/2(1/2):326-336. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%