Three types of Ce0.45Zr0.45La0.1O1.95 mixed oxides were prepared by H2O2-assisted precipitation using ZrOCO3, ZrO(NO3)2, and Zr(NO3)4 as precursors. The Pd/Ce0.45Zr0.45La0.1O1.95 three-way catalysts were prepared by the wet impregnation and characterized by the X-ray diffraction (XRD), Raman spectroscopy, nitrogen adsorption, X-ray photoelectron spectroscopy (XPS), temperature-programmed reduction (TPR), and oxygen storage capacity. XRD and Raman spectroscopy results showed that the use of ZrOCO3 or ZrO(NO3)2 gave a CeO2-ZrO2 mixed oxide with a cubic phase of high thermal stability, while an extra t″-phase was observed in the aged Pd/Ce0.45Zr0.45La0.1O1.95 catalyst prepared using Zr(NO3)4. The activities of the three catalysts were evaluated using simulated exhaust gas under working conditions. The Pd/Ce0.45Zr0.45La0.1O1.95 catalyst prepared using ZrOCO3 as precursor gave the best activities for C3H8, CO, and NO conversion. The use of ZrOCO3 as precursor was better suited for the formation of Ce3+and more favorable for the homogeneous insertion of Zr4+ and La3+ into the CeO2 lattice, which resulted in better thermal stability and enhanced redox properties of the Pd/Ce0.45Zr0.45La0.1O1.95 catalyst.
参考文献
| [1] | Ka?par J;Fornasiero P;Graziani M .[J].Catalysis Today,1999,50:285. |
| [2] | 崔亚娟,何胜楠,方瑞梅,史忠华,龚茂初,陈耀强.整体式Pd/La2O3-Al2O3和Pd/CeO2-ZrO2-Y2O3催化剂上汽油车尾气净化性能的比较[J].催化学报,2012(06):1020-1026. |
| [3] | 沈美,龚茂初,袁书华,郭家秀,陈耀强.表面活性剂对CeZrYO储氧材料性能的影响[J].催化学报,2007(12):1067-1071. |
| [4] | 姚艳玲,史忠华,宋为聪,袁书华,龚茂初,陈耀强.满足欧V排放标准的汽油车中偶催化剂[J].催化学报,2008(04):316-318. |
| [5] | 赵梅;王海容;陈山虎;姚艳玲 龚茂初 陈耀强 .[J].催化学报,2010,31:429. |
| [6] | Fan J;Weng D;Wu XD;Wu XD;Ran R .Modification of CeO2-ZrO2 mixed oxides by coprecipitated/impregnated Sr: Effect on the microstructure and oxygen storage capacity[J].Journal of Catalysis,2008(1):177-186. |
| [7] | Hori C E;Permana H;Simon Ng K Y;Brenner A More K Rahmoeller K M Belton D .[J].Applied Catalysis B:Environmental,1998,16:105. |
| [8] | Rossignol S;Madier Y;Duprez D .[J].Catalysis Today,1999,50:261. |
| [9] | Letichevsky S;Tellez CA;de Avillez RR;da Silva MIP;Fraga MA;Appel LG .Obtaining CeO2-ZrO2 mixed oxides by coprecipitation: role of preparation conditions[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2005(3/4):203-210. |
| [10] | Woodhead J L .[P].US 4231893,1980. |
| [11] | Scholes FH;Soste C;Hughes AE;Hardin SG;Curtis PR .The role of hydrogen peroxide in the deposition of cerium-based conversion coatings[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2006(4):1770-1780. |
| [12] | 张磊,郑灵敏,郭家秀,吴冬冬,龚茂初,王健礼,陈耀强.氧化共沉淀法制备Ce0.65Zr0.25Y0.1O1.95的结构转化过程[J].物理化学学报,2008(08):1342-1346. |
| [13] | Wang Q Y;Li G F;Zhao B;Shen M Q Zhou R X .[J].Applied Catalysis B:Environmental,2010,101:150. |
| [14] | Guo Y;Lu G Z;Zhang Z G;Zhang S H Qi Y Liu Y .[J].Catalysis Today,2007,126:296. |
| [15] | Fornasiero P;Balducci G;Di Monte R;Ka?par J Sergo V Gubitosa G Ferrero A Graziani M .[J].Journal of Catalysis,1996,164:173. |
| [16] | Reddy BM.;Khan A.;Yamada Y.;Kobayashi T.;Loridant S.;Volta JC. .Raman and X-ray photoelectron spectroscopy study of CeO2-ZrO2 and V2O5/CeO2-ZrO2 catalysts[J].Langmuir: The ACS Journal of Surfaces and Colloids,2003(7):3025-3030. |
| [17] | Si R;Zhang Y W;Li Sh J;Lin B X Yan Ch H .[J].Journal of Physical Chemistry B,2004,108:12481. |
| [18] | Zhao B;Li G F;Ge Ch H;Wang Q Y Zhou R X .[J].Applied Catalysis B:Environmental,2010,96:338. |
| [19] | Wang J;Wen J;Shen M Q .[J].Journal of Physical Chemistry C,2008,112:5113. |
| [20] | Theocharis C R;Kyriacou G;Christophidou M .[J].Adsorption-Journal of the International Adsorption Society,2005,11:763. |
| [21] | Rao G R .[J].Bulletin of Materials Science,1999,22:89. |
| [22] | Bruce L A;Hoang M;Hughes A E;Turner T W .[J].Applied Catalysis A:General,1996,134:351. |
| [23] | Fornasiero P.;Rao GR.;Kaspar J.;Meriani S.;Trovarelli A. Graziani M.;Dimonte R. .RH-LOADED CEO2-ZRO2 SOLID SOLUTIONS AS HIGHLY EFFICIENT OXYGEN EXCHANGERS - DEPENDENCE OF THE REDUCTION BEHAVIOR AND THE OXYGEN STORAGE CAPACITY ON THE STRUCTURAL PROPERTIES[J].Journal of Catalysis,1995(1):168-177. |
| [24] | Liotta L F;Longo A;Macaluso A;Martorana A Pantaleo G Venezia A M Deganello G .[J].Applied Catalysis B:Environmental,2004,48:133. |
| [25] | Liu L Ch;Wei T;Zi X H;He H Dai H X .[J].Catalysis Today,2010,153:162. |
| [26] | Dong F;Suda A;Tanabe T;Nagai Y Sobukawa H Shinjoh H Sugiura M Descorme C Duprez D .[J].Catalysis Today,2004,93-95:827. |
| [27] | Weng X L;Perston B;Wang X Z;Abrahams I, Lin T, Yang Sh F. Evans J R G, Morgan D J, Carley A F, Bowker M, Knowles J C, Rehman I, Darr J A .[J].Applied Catalysis B:Environmental,2009,90:405. |
| [28] | 蔡黎,赵明,皮展,龚茂初,陈耀强.Ce-Zr-La-Al2O3的制备及负载的单Pd三效催化剂[J].催化学报,2008(02):108-112. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%