以C2H4为碳源、Ni-Cu合金作催化剂,采用化学气相沉积法在蜂窝状堇青石表面生长纳米炭纤维(CNFs),获得压缩强度为50.0 MPa的纳米炭纤维/蜂窝堇青石复合材料.在堇青石表面蜂窝腔内生长的CNFs直径为20nm~30nm,CNFs之间相互交织形成5μm厚的纤维层,CNFs的质量分数为25.3%.金属Cu的掺杂对Ni-Cu合金的颗粒尺寸产生重要影响,进而影响CNFs的生长速率、纤维层厚度及其微结构.所合成CNFs的石墨化程度不高,在蜂窝堇青石中生长纳米炭纤维可以把其压缩强度从10MPa增加到50 MPa.

A carbon nanofiber ( CNF)/honeycomb cordierite composite with a compressive strength of 50 MPa was prepared by chemical vapor deposition,using C2H4 as the carbon source and Ni-Cu alloy as the catalyst.The CNFs with a diameter of 20-30 nm in the cells of the honeycomb interweave with each other to form a 5 μm- thick layer.The CNF content is 25.3 wt%.The Cu has remarkable effects on the particle size of the Ni-Cu alloy,which further affects the growth rate,loading level and nanostructures of the CNFs.The CNFs are not well graphitized and the insertion of the CNFs into the honeycomb can increase its compressive strength from 10 to 50MPa.

参考文献

[1] Enrique Garcia-Bordeje;Ingvar Kvande;De Chen;Magnus Ronning .Carbon Nanofibers Uniformly Grown on γ-Alumina Washcoated Cordierite Monoliths[J].Advanced Materials,2006(12):1589-1592.
[2] Cebollada P A R;Enrique G B .Optimisation of physical properties of γ-alumina coating microreactors used for the growth of a carbon nanofiber layer[J].Chemical Engineering Journal,2009,149(1-3):447-454.
[3] Lucia Martmez-Latorre;Sabino Armenise;Enrique Garcia-Bordeje .Temperature-mediated control of the growth of an entangled carbon nanofiber layer on stainless steel micro-structured reactors[J].Carbon: An International Journal Sponsored by the American Carbon Society,2010(7):2047-2056.
[4] Zhang J;Liu X;Blume R et al.Surface-modified carbon nanotubes catalyze oxidative dehydrogenation of n-Butane[J].Science,2008,322(5898):73-77.
[5] Yoon SH;Lim S;Hong SH;Qiao WM;Whitehurst DD;Mochida I;An B;Yokogawa K .A conceptual model for the structure of catalytically grown carbon nano-fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,2005(9):1828-1838.
[6] Baker RTK;Rodriguez N;Mastalir A;Wild U;Schlogl R;Wootsch A;Paal Z .Platinum/graphite nanofiber catalysts of various structure: Characterization and catalytic properties[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,2004(38):14348-14355.
[7] Tiejun Zhao;Ingvar Kvande;Yingda Yu .Synthesis of Platelet Carbon Nanofiber/Carbon Felt Composite on in Situ Generated Ni-Cu Nanoparticles[J].The journal of physical chemistry, C. Nanomaterials and interfaces,2011(4):1123-1133.
[8] Sternmet CP;Meeuwse A;van der Schaaf J;Kuster BFM;Schouten JC .Gas-liquid mass transfer and axial dispersion in solid foam packings[J].Chemical Engineering Science,2007(18/20):5444-5450.
[9] Jitendra Kumar Chinthaginjala;Johannes Hendrik Bitter;Leon Lefferts .Thin layer of carbon-nano-fibers (CNFs) as catalyst support for fast mass transfer in hydrogenation of nitrite[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2010(1/2):24-32.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%