室温下,将能量为250 keV He+离子注入z切钽酸锂单晶,注量范围为5.0×1014~5.0×1016He+/cm2,应用三维轮廓仪、X射线衍射(XRD)、紫外可见(UV-Vis)光学吸收谱对未注入和注入样品进行了表征和分析.分析结果表明,在注量达到5.0×1016 He+/cm2时,样品表面出现大量凸起条纹,同时晶格沿着[001]方向出现明显肿胀,吸收边则表现出明显的注量相关性.注入样品在空气中放置60 d后,最高注量的样品表面原来凸起的条纹变为细长的裂纹,晶格应变及光学吸收边均出现较大的恢复.讨论了样品表面形貌、晶格应变和光学吸收边与He行为的关系.
参考文献
[1] | BRUEL M.Nucl Instr and Meth B,1996,108(3):313. |
[2] | TONG Q Y,GOSELE U M.Adv Mater,1999,11(17):1409. |
[3] | RADU I,SZAFRANIAK I,SCHOLZ R,et al.Ferroelectric Thin Films Xi[M].USA:Materials Research Society,2003:337-342. |
[4] | L1U W,ZHAN D,MA X.J Vac Sci Technol B,2008,26(1):206. |
[5] | SIMPSON T W,MITC HE LL I V,ESTE G O,et al.Nucl Instr and Meth B,1999,148(4):381. |
[6] | TERREAULT B.Phys Status Solidi A,2007,204(7):2129. |
[7] | HARTMANN M,TRINKAUS H.Phys Rev Lett,2002,88(5):055505. |
[8] | KLING A,da SILVA M E SOARES J C,et al.Nucl Instr and Meth B,2001,175:394. |
[9] | OFAN A,GAATHON O,ZHANG L,et al.Phys Rev B,201l,83(6):064104. |
[10] | OFAN A,GAATHON O,ZHANG L,et al.Phys Rev B,2010,82(10):104113. |
[11] | ROTH R M,DJUKIC D,LEE Y S,et al.Appl Phys Lett,2006,89(11):112906. |
[12] | GLAVAS E,ZHANG L,CHANDLER P J,et al.Nucl Instr and Meth B,1988,32(4):45. |
[13] | ZIEGLER J F.SRIM 2008[EB/OL].[2011-05-20].http://www.srim.org/. |
[14] | GOPALAN V,DIEROLF V,SCRYMGEOUR D A.Annual Review of Materials Research.Palo Alto:Annual Reviews,2007:449--489. |
[15] | TRINKAUS H.J Nucl Mater,2003,318:234. |
[16] | JIA Xiujun,ZHANG Chonghong,ZHANG Liqing,et al.Nuclear Physics Review,2011,28(3):332 (in Chinese).(贾秀军,张崇宏,张丽卿,等.原子核物理评论,2011,28(3):332.) |
[17] | ZANG Hang,WANG Zhiguang,WEI Kongfang,et al.Nuclear Physics Review,2010,27(1):87 (in Chinese).(臧航,王志光,魏孔芳,等.原子核物理评论,2010,27(1):87.) |
[18] | KIM I G,TAKEKAWA S,FURUKAWA Y,et al.J Cryst Growth,2001,229(4):243. |
[19] | SCHNATTERLY S E.Phys Rev,1965,140(4):A1364. |
[20] | BALSLEV I.Phys Rev,1966,143(2):636. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%