采用新型的内孔电刷镀技术对失效的发动机缸套内表面进行了再制造.利用SEM,XRD,TEM,显微硬度计和CETR显微磨损试验机,考察了不同相对运动速度下电刷镀镍镀层的组织结构和性能,并与传统电镀Watts Ni进行了对比.结果表明:镍镀层均为面心立方结构,但电镀Watts Ni镀层表面粗糙,择优取向为(200)面,而应用电刷镀制备的镍镀层表面平整致密,无针孔、麻点等缺陷,择优取向为(111)面.随着相对运动速度从0.25m/s增加到1.00m/s,电刷镀层的(200)面择优取向逐渐降低,而(111)面择优取向逐渐增大;镀层的硬度由HV420增大到HV600,镀层的磨损失重由8.7mg降低到6mg.
参考文献
[1] | 徐滨士;朱绍华.表面工程的理论与技术[M].北京:国防工业出版社,2010 |
[2] | 徐滨士.装备再制造工程的理论与技术[M].北京:国防工业出版社,2007 |
[3] | XU Bin-shi.Nano surface engineering and remanufacture engineering[J].中国有色金属学会会刊(英文版),2004(z1):1-5. |
[4] | WANG Xiao-he;LV Biao;HU Zhen feng et al.Corrosion resistance in sodium chloride solution of Ni-Co-P electro-brush amorphous coatings to replace hard chromium coatings[J].Physics Procedia,2013,50:191-198. |
[5] | XU Bin-shi;WANG Hai dou;DONG Shi-yun et al.Electrodeposition nickel silica nano composites coating[J].Electrochemistry Communications,2005,7(06):572-575. |
[6] | 徐滨士.再制造工程与自动化表面工程技术[J].金属热处理,2008(01):9-14. |
[7] | XU Bin-shi .Development of surface engineering in China[J].Surface Engineering,2010,26(1-2):129-132. |
[8] | 张斌,徐滨士,董世运,吴斌.自动化n-SiC/Ni复合电刷镀层的高温摩擦性能研究[J].材料工程,2008(01):54-57. |
[9] | 胡振峰 .内孔电刷镀纳米晶镍镀层制备技术及其在再制造产业中的应用[D].北京:装甲兵工程学院,2010. |
[10] | 胡振峰,汪笑鹤,吕镖,徐滨士.自动化电刷镀技术在发动机缸体再制造中的应用[J].中国表面工程,2012(04):27-30. |
[11] | S. Sopok;C. Rickard;S. Dunn .Thermal-chemical-mechanical gun bore erosion of an advanced artillery system part one: theories and mechanisms[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2005(1/4):659-670. |
[12] | Bobzin K;Ernst F;Richardt K;Schlaefer T;Verpoort C;Flores G .Thermal spraying of cylinder bores with the Plasma Transferred Wire Arc process[J].Surface & Coatings Technology,2008(18):4438-4443. |
[13] | Akio Katsuki;Hiromichi Onikura;Takao Sajima;Akira Mohri;Tomoyuki Moriyama;Yutaka Hamano;Hiroshi Murakami .Development of a practical high-performance laser-guided deep-hole boring tool: Improvement in guiding strategy[J].Precision Engineering,2011(2):221-227. |
[14] | 吕镖,胡振峰,汪笑鹤,徐滨士.电流密度对柔性摩擦辅助电沉积镍镀层质量的影响[J].中国有色金属学报,2014(01):137-144. |
[15] | WATANABE T.Nano plating[M].Amsterdam:Elsevier Ltd,2004 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%