基于某汽车公司提出的曲面焊接设计需求,研究了变形对焊接组织的影响.选用熔化极气体保护焊在奥氏体不锈钢304L的T型接头和变形钢板上焊接,寻求合理的变形后焊接参数并观察变形对焊接组织的影响.得到合理焊接参数为焊枪速率4mm/s,送丝速率2.5m/min,电压17V.在T型和变形后焊接中,焊趾分别处于应变为0％,30％的区域,观察到变形后焊接件中熔化区和部分熔化区范围减小,焊接接头碳化物沉积和晶间铁素体数量减小.304L变形后焊接获得了更为均匀的接头组织.
This subject was raised by an automotive company.Based on the welding design on the curved surface,the effect of prior deformation on the weld structure was studied.Metal active-gas welding was used on the T-joint and pre-deformed plates of austenitic stainless steel 304L to find the proper welding parameters and observe the effect of prior deformation on the microstructure.The proper parameters acquired are:the speed of the torch is 4mm/s,the speed of delivery of welding wire is 2.5m/min and the voltage is 17V.In the T-joint and pre-deformed joint,the weld toes are in the zone with strain of 0％ and 30％.In the pre-deformed welding specimen,it was observed that the fusion zone and partially melted zone are narrowed,carbide precipitation and ferrites are found less.In all,the microstructure in the pre-deformed weld joints on 304L is more uniform.
参考文献
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%