研究了Mg 2Zn Mn-0.5Nd镁合金不同挤压温度对其制品组织和性能的影响及作用机理.结果显示:挤压温度从340℃提高到420℃时,合金的室温伸长率可从14%左右提高到26%以上,伴随强度明显下降.挤压温度从340℃降低到260℃时,合金的伸长率也提升到19%,而强度减弱不明显.分析表明:合金的晶粒尺寸和织构强弱等因素,共同决定该合金挤压制品的室温力学性能.
参考文献
[1] | FATERMI VARZANEH S M,ZAREI HANZAK A,BELADI H.Dynamic recrystallization in AZ31 magnesium alloy[J].Materials Science and Engineering A,2007,V456:52-57.,2007. |
[2] | CHEN Q,SHU D Y,ZHAO Z D,et al .Microstructure development and tensile mechanical properties of Mg-Zn RE-Zr magnesium alloy[J].Materials & Design,2012,40 |
[3] | 张丁非,耿青梅,杨绪盛,等.新型复合挤压工艺中温度对AZ61组织和性能的影响[J].材料工程,2014,(7):1-4.ZHANG Ding-fei,GENG Qing-mei,YANG Xu-sheng,et al.Effects of temperature in the new compound extrusion on microstructures and properties of AZ61[J].Journal of Materials Engineering,2014,(7):1-4.,2014. |
[4] | 汪清,王敬丰,黄崧,李琳俊楠,耿铁,潘复生.加工工艺对AZ61镁合金拉压不对称性的影响[J].材料工程,2013(11):57-61,88. |
[5] | 吕滨江,彭建,童小山,等 .挤压温度对Mg-2.0Zn-0.3Zr-0.9Y新型镁合金组织和性能的影响[J].稀有金属材料与工程,2013,42(4):841-844.LV Bin-jiang,PENG Jian,TONG Xiao-shan,et al.Effect of extruding temperature on microstructure and mechanical properties of Mg-2.0Zn-0.3Zr-0.9Y alloy[J].Rare Metal Materials and Engineering,2013,42(4):841-844.,2013. |
[6] | 梁书锦,王欣,刘祖岩,王尔德.AZ31镁合金不同温度挤压后组织性能研究[J].稀有金属材料与工程,2009(07):1276-1279. |
[7] | ZHANG B P,GENG L,HUANG L J .Enhanced mechanical properties in fine grained Mg-1.0Zn-0.5Ca alloys prepared by extrusionat different temperatures[J].Scripta Materialia,2010,63 |
[8] | BOHLEN J,LETZIG D,JAUBER K U.Influence of process parameters on the mechanical properties of rolled magnesium ZM21-sheets[J].Metals and Materials Society,2007,(5):95-100.,2007. |
[9] | MEHTEDI M E,BALLONI L,SPIGARELLI S,et al .Hot work ability and constitutive equations of ZM21magnesium alloy[J].Key Engineering Materials,2008,367 |
[10] | SWIOSTEK J,LETZIG D,KAINER K U .Hydrostatic extrusion at 100℃ and its effect on the grain size and mechanical properties of magnesium alloy[J].Metal Science and Heat Treatment,2006,48:499-503.,2006. |
[11] | LATWELL D,BARNETT M R .Extrusion limits of magnesium alloys[J].Metallurgical and Materials Transactions A,2007,38(12):3032-3041.,2007. |
[12] | BARNETT M R,ATWELL D L,BEER A G.Grain size in Mg alloys:recrystallization and mechanical consequences[J].Materials Science Forum,2007,V558-559:433-440.,2007. |
[13] | 王亚霄,付俊伟,杨院生.Nd添加对AZ80镁合金显微组织及力学性能的影响[J].中国有色金属学报(英文版),2012(06):1322-1328. |
[14] | ZHAO Yazhong,PAN Fusheng,PENG Jian,WANG Weiqing,LUO Suqin.Effect of neodymium on the as-extruded ZK20 magnesium alloy[J].稀土学报(英文版),2010(04):631-635. |
[15] | WANGB,GUANSK,WANG J,et al .Effects ofNdon microstructures and properties of extruded Mg-2Zn-0.46Y-xNd alloys for stent application[J].Materials Science and Engineering B,2011,176(20):1673-1678.,2011. |
[16] | 钟皓,张慧,翁文凭,陈琦,詹志强,闫蕴琪.热挤压工艺对AZ31镁合金组织与力学性能的影响[J].金属热处理,2006(08):79-82. |
[17] | 陈振华,夏伟军,程永奇,傅定发.镁合金织构与各向异性[J].中国有色金属学报,2005(01):1-11. |
[18] | 陈振华.变形镁合金[M].北京:化学工业出版社,2005.CHEN Zhen-hua.Wrought Magnesium Alloy[M].Beijing:Chemical Industry Press,2005.,2005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%