比较分析了复合模型法和θ投影法在描述P92钢蠕变行为时的差异.结果表明:两者在拟合P92钢蠕变-时间关系曲线上均有较高的精度,但在描述蠕变速率-时间曲线上,θ投影法呈现较大的误差而复合模型则有良好的关联结果.在外推蠕变速率时,θ投影法的外推结果发生较大偏折,而复合模型的预测结果更接近实际变化趋势.基于蠕变曲线外推持久寿命的结果表明:5%~50%范围内的断裂应变对寿命预测结果影响较小,两种模型预测的持久寿命值之间也相差不大.
参考文献
[1] | LARSON F R;MILLER J .A time-temperature relationship for rupture and creep stress[J].ASME Trans,1952,74(5):765-771. |
[2] | ORR R L;SHERBY O D;DORN J E .Correlation of rupture data for metals at elevated temperatures[J].ASME Trans,1954,76(1):113-128. |
[3] | 刘春慧,程从前,赵杰,祝志超,马海涛.MHZ常数在耐热钢持久性能预测中的应用[J].材料工程,2012(10):12-16. |
[4] | 张俊善.材料强度学[M].哈尔滨:哈尔滨工业大学出版社,2004 |
[5] | Woo-Gon Kim;Song-Nan Yin;Yong-Wan Kim .Creep characterization of a Ni-based Hastelloy-X alloy by using theta projection method[J].Engineering Fracture Mechanics,2008(17):4985-4995. |
[6] | 孙海生,徐彤,关凯书.Omega蠕变寿命评估方法及应用[J].压力容器,2012(09):19-23. |
[7] | GRAHAM A;WALLES K F A .Relationships between long and short-time creep and tensile properties of a commercial alloy[J].Journal of the Iron and Steel Institute of Japan(in Japanese),1955,179(12):105-120. |
[8] | 杨王玥;李志文 .θ法预测12Cr1MoV钢主蒸汽管道材料剩余寿命[J].金属学报,1999,35(7):721-725. |
[9] | S. Ibarra;R. R. Konet .Life Assessment of 1 1/4 Cr-1/2 Mo steel catalytic reformer furnace tubes using the MPC omega method[J].Journal of pressure vessel technology,1995(1):19-23. |
[10] | OIKAWA H;MARUYAMA K .Prediction of long-term creep curves[J].Fusion Engineering and Design,1992,19(4):321-328. |
[11] | Rolf Sandstrom .Basic model for primary and secondary creep in copper[J].Acta materialia,2012(1):314-322. |
[12] | Luca Esposito;Nicola Bonora .Primary Creep Modeling Based on the Dependence of the Activation Energy on the Internal Stress[J].Journal of pressure vessel technology,2012(6):061401-1-061401-6. |
[13] | CHEN G L;GUO H;SUN J Y;etal .Extrapolation model of high temperature creep for 12CrMoV steel[J].Pressure Vessel Technology,2011,28(8):11-15. |
[14] | 黄硕,万敏,黄霖,迟彩楼,季秀升.铝合金蠕变试验及本构模型建立[J].航空材料学报,2008(01):93-96. |
[15] | RAY A K;DIWAKAR K;PRASAD B N;etal .Long term creep-rupture behavior of 813K exposed 2.25-1Mo steel between 778 and 873K[J].Materials Science and Engineering A,2007,454-455(25):124-131. |
[16] | 刘春慧 .超(超)临界用钢高温持久寿命外推方法的比较分析[D].大连理工大学,2013. |
[17] | KIMURA K;SAWADA K;KUBO K;etal.Influence of stress on degradation and life prediction of high strength ferritic steels[A].USA:ASME,2004:11-18. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%