采用一种超声辅助激光钎焊的方法,对低熔点的Al基钎料在TiNi形状记忆合金合金表面进行了润湿性实验.研究结果表明:随超声时间增加,钎料铺展面积先增大后减少,润湿角先减小后增大.钎料润湿前沿存在Al2Si,Al3Si,AlSi等相,钎料熔滴中心靠近界面处,AlSi和AlSiTi相的晶粒尺寸及其中Si元素的含量均随超声时间增加而逐渐增大;随着激光功率的降低,钎料铺展面积逐渐降低,润湿角逐渐增大,在钎料熔滴中心靠近界面处生长出宽度小于10μm的AlSi(Ti,Ni)金属间化合物.当超声振动时间为1.0s,激光功率470W,母材表面粗糙度为0.03μm时,实验获得的最大铺展面积为106.45mm2,最小润湿角为16°.

参考文献

[1] Falvo A;Furgiuele FM;Maletta C.Laser welding of a NiTi alloy: Mechanical and shape memory behaviour[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20051/2(1/2):235-240.
[2] Vieira, L.A.;Fernandes, F.M.B.;Miranda, R.M.;Silva, R.J.C.;Quintino, L.;Cuesta, A.;Oca?a, J.L..Mechanical behaviour of Nd:YAG laser welded superelastic NiTi[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201116/17(16/17):5560-5565.
[3] J. Pouquet;R. M. Miranda;L. Quintino;S. Williams.Dissimilar laser welding of NiTi to stainless steel[J].The International Journal of Advanced Manufacturing Technology,20121/4(1/4):205-212.
[4] R.H. Shiue;S.K. Wu.Infrared brazing of Ti_50Ni_50 shape memory alloy using two Ag-Cu-Ti active braze alloys[J].Intermetallics,20066(6):630-638.
[5] 李红;栗卓新;汪应玲;冯吉才.TiNi形状记忆合金不锈钢的瞬时液相扩散焊[J].稀有金属材料与工程,2011(8):1382-1386.
[6] 王蔚;陈俐;赵兴科;黄继华;李宏光;董兴文.预置填充稀土激光焊接对TiNi形状记忆合金功能性的影响[J].稀有金属材料与工程,2008(10):1819-1823.
[7] 许志武;闫久春;钟利;杨士勤.铝合金超声波钎焊过程中液态钎料的填缝及界面润湿行为[J].材料工程,2010(10):1-4,8.
[8] 陈树海;李俐群;陈彦宾.铝/钛异种合金激光熔钎焊接头界面特性[J].中国有色金属学报,2008(6):991-996.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%