研究T700/5224复合材料在湿热环境和15#液压油、4010#合成航空润滑油、RP-3航空煤油和AHC-1水基型清洗剂4种飞机上常用的化学介质中的老化行为、实验不同时间后的吸湿量及力学性能.采用红外光谱(IR)和动态力学(DMA)分析T700/5224复合材料在介质老化过程中的化学变化和玻璃化转变温度Tg.结果表明:在80℃-85%RH的湿热环境中实验1000h后吸湿量为1.05%,在80℃-100%RH的湿热环境中实验1000h后的吸湿量为1.35%;T700/5224复合材料湿热老化后,剪切性能随老化时间变化不大,弯曲性能下降较大,开孔拉伸性能变化较大,但总体上并没有降低,而开孔压缩性能一直缓慢下降.介质老化对T700/5224复合材料的力学性能影响不大,AHC-1水基型清洗剂对其影响大于其他3种介质,T700/5224复合材料在AHC-1水基型清洗剂中浸泡45天后其玻璃转变温度Tg下降10℃.
The aging properties,absorption and mechanical properties of T700/5224 composites which were in hygrothermal environment and in 15# hydraulic oil,4010# lubricating oil,RP-3 kerosene and AHC-1 cleaner were studied.The properties'changes and Tg of the T700/5224 composite were ana-lyzed by infrared analysis (IR)and dynamic mechanical analysis (DMA).The results show that the absorption is 1.05% in environment of 80℃-85%RH,and 1.35% in environment of 80℃-100%RH. Shear strength is not changed obviously,but flexural strength decreases greatly.Open-hole tensile strength changes a lot,but on the whole,not decreases.Open-hole compression strength is always gradually decreasing.There is no evident impact on mechanical properties of composite by chemical solutions.The effect of AHC-1 cleaner on T700/5224 composite is bigger than the other three media, Tg declines 10℃ after soaking in AHC-1 cleaner for 45 days.
参考文献
| [1] | 唐义号;陈群志;关志东;常铁军;王逾涯.缺陷及湿热环境对复合材料层压板力学性能的影响[J].腐蚀科学与防护技术,2005(z1):457-459. |
| [2] | 彭雷;张建宇;鲍蕊;费斌军.湿热、紫外环境对T300/QY8911复合材料孔板静力性能的影响[J].复合材料学报,2009(3):18-23. |
| [3] | 冯宇;何宇廷;安涛;崔荣洪;邵青;范超华.湿热环境对航空复合材料加筋板压缩屈曲和后屈曲性能的影响[J].材料工程,2015(5):81-88. |
| [4] | 姚宇超;许希武;毛春见.湿热环境下开孔复合材料层合板的强度[J].材料科学与工程学报,2015(3):425-431. |
| [5] | 高禹;王钊;陆春;包建文;宋恩鹏;董尚利.高性能树脂基复合材料典型空天环境下动态力学行为研究现状[J].材料工程,2015(3):106-112. |
| [6] | 余治国;杨胜春;宋笔锋.T700和T300碳纤维增强环氧树脂基复合材料耐湿热老化性能的对比[J].机械工程材料,2009(6):48-51. |
| [7] | L Rezgani;B Bachir Bouiadjra;M Belhouari.Effect of composite hygrothermal aging on the SIF variation in bonded composite repair of aircraft structures[J].Journal of Reinforced Plastics and Composites,201024(24):3631-3636. |
| [8] | 冯青;李敏;顾轶卓;刘洪新;张佐光.不同湿热条件下碳纤维/环氧复合材料湿热性能实验研究[J].复合材料学报,2010(6):16-20. |
| [9] | 刘旭;陈跃良;霍武军;徐丽;王莉.碳纤维复合材料湿热老化加速关系[J].南京航空航天大学学报,2014(3):382-388. |
| [10] | 刘淑峰;程小全;包建文.湿热环境对树脂基复合材料性能影响的分析[J].高分子材料科学与工程,2014(9):183-190. |
| [11] | 陈达;肇研;罗云烽;洪旭辉.循环湿热环境下碳纤维复合材料界面性能[J].材料科学与工艺,2012(06):1-6. |
| [12] | 张利军;肇研;罗云烽;段跃新.湿热循环对CCF300/QY8911复合材料界面性能的影响[J].材料工程,2012(2):25-29,49. |
| [13] | 谢可勇;李晖;孙岩;王登霞;李倩倩.湿热老化对纤维增强树脂基复合材料性能的影响及其机理[J].机械工程材料,2014(8):1-5,107. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%