采用嵌段共聚物增韧双马来酰亚胺(BMI)树脂体系,制备双马来酰亚胺树脂底胶(双马底胶),该底胶的黏附性、铅笔硬度、抗冲击、耐环境、耐老化性能等技术指标满足GJB1388规范要求.采用DSC,TG,DMA测试对双马底胶性能热性能进行表征.结果表明:该底胶具有良好的耐热性,200℃固化后玻璃化转变温度为238℃,5％热失重温度为384℃,230℃热处理后玻璃化转变温度高达268℃,5％热失重温度为407℃.双马底胶和双马胶膜配合使用后粘接强度提高,当与J-188双马胶膜配合使用时,剥离强度提高到l07％,常温和高温剪切强度可提高10％.该底胶也可与其他双马结构胶膜配合使用,适用于金属之间或双马复合材料与金属之间的粘接.
参考文献
| [1] | 王德志;曲春艳;冯浩.金属橡胶热硫化型底胶的研制[J].粘接,2010(4):54-57. |
| [2] | 郑洪光;邹德荣.金属用底胶表面处理的工艺研究[J].粘接,2012(11):64-66. |
| [3] | LUCAS F.M.DA SILVA;R.D.ADAMS.Measurement of the mechanical properties of structural adhesives in tension and shear over a wide range of temperatures[J].Journal of Adhesion Science and Technology: The International Journal of Theoredtical and Basic Aspects of Adhesion Science and Its Applications in All Areas of Technology,20052(2):109-141. |
| [4] | Lucas F.M.da Silva;R.D.Adams;M.Gibbs.Manufacture of adhesive joints and bulk specimens with high-temperature adhesives[J].International Journal of Adhesion & Adhesives,20041(1):69-83. |
| [5] | Anderson, B.J..Thermal stability of high temperature epoxy adhesives by thermogravimetric and adhesive strength measurements[J].Polymer Degradation and Stability,201110(10):1874-1881. |
| [6] | 陈丽敏;焦婷;雷安民;杨胜春.新型双马结构胶J299性能试验研究[J].科学技术与工程,2014(6):97-100. |
| [7] | 王德志;曲春艳;张杨;汪成.耐热200℃双马改性环氧结构胶膜的研究[J].中国胶粘剂,2005(4):6-9. |
| [8] | 曲春艳;王德志;冯浩;张杨;毛勇;王海民.双马来酰亚胺基碳纤维复合材料胶接用结构胶膜[J].航空制造技术,2007(z1):118-122. |
| [9] | 李洪峰;王德志;赵立伟;曲春艳;毛勇;王海民.聚酰胺酰亚胺对BMI/DP共聚树脂的增韧研究[J].中国胶粘剂,2013(7):5-8,17. |
| [10] | 代晓瑛;雷兴平.J-188结构胶膜对聚醚醚酮复合材料胶接性能研究[J].工程塑料应用,2013(12):91-93. |
| [11] | 李洪峰;周恒;王德志;曲春艳;赵彤;顾继友.双邻苯二甲腈树脂胶黏剂的研究[J].材料工程,2014(10):21-26. |
| [12] | 郭平军;梁国正;张增平.胶粘剂在航天工业中的应用[J].中国胶粘剂,2009(3):56-60. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%