采用微滴包埋拉出测试的方法,分别测定两种不同表面性质中间相沥青基碳纤维与环氧树脂的界面剪切强度(σIFSS).从负载-位移曲线读取树脂小球从碳纤维上脱落时的脱粘力值,并利用扫描电子显微镜观察了脱粘树脂小球和碳纤维的状态,然后定量地计算出σIFSS的平均值以及其标准方差、离散系数,并讨论了σIFSS同树脂小球的长度与直径、纤维直径的关系,研究发现:所测量的界面剪切强度值与环氧树脂小球的长径比正比,与纤维直径成反比,与环氧树脂小球的长度和纤维直径的比值反比,与环氧树脂小球的直径和纤维直径的比值成反比.
参考文献
| [1] | Sanchez-Adsuar MS.;Linares-Solano A.;Cazorla-Amoros D.;Ibarra-Rueda L..Influence of the nature and the content of carbon fiber on properties of thermoplastic polyurethane-carbon fiber composites[J].Journal of Applied Polymer Science,200310(10):2676-2683. |
| [2] | Serge Zhandarov;Edith Mader.Characterization of fiber/matrix interface strength: applicability of different tests, approaches and parameters[J].Composites science and technology,20051(1):149-160. |
| [3] | X. Gao;R.E. Jensen;S.H. McKnight.Effect of colloidal silica on the strength and energy absorption of glass fiber/epoxy interphases[J].Composites, Part A. Applied science and manufacturing,201111(11):1738-1747. |
| [4] | Wang, H.;Li, W.;Ren, D.;Yu, Y..An improved microbond test method for determination of the interfacial shear strength between carbon fibers and epoxy resin[J].Polymer Testing,20138(8):1460-1465. |
| [5] | Michael Q. Tran;Kingsley K.C. Ho;Gerhard Kalinka;Milo S.P. Shaffer;Alexander Bismarck.Carbon fibre reinforced poly(vinylidene fluoride): Impact of matrix modification on fibre/polymer adhesion[J].Composites science and technology,20087/8(7/8):1766-1776. |
| [6] | Liu, B.;Liu, Z.;Wang, X.;Zhang, G.;Long, S.;Yang, J..Interfacial shear strength of carbon fiber reinforced polyphenylene sulfide measured by the microbond test[J].Polymer Testing,20134(4):724-730. |
| [7] | Fei Deng;Weibang Lu;Haibo Zhao.The properties of dry-spun carbon nanotube fibers and their interfacial shear strength in an epoxy composite[J].Carbon: An International Journal Sponsored by the American Carbon Society,20115(5):1752-1757. |
| [8] | Fiber/epoxy Interfacial Shear Strength Measured By The Microdroplet Test[J].Composites science and technology,20092(2):p.245. |
| [9] | Nak-Sam Choi;Joo-Eon Park.Fiber/matrix interfacial shear strength measured by a quasi-disk microbond specimen[J].Composites science and technology,200910(10):1505-1515. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%