采用光学显微镜、扫描电子显微镜、万能力学试验机等测试分析手段,研究中间退火对5182铝合金完全退火态(5182-O)板材组织和性能的影响.结果表明:与未经中间退火的5182-O板材相比,中间退火后的5182-O板材晶粒尺寸过于细小,金属间化合物破碎不充分、尺寸大,弥散析出相数量少;屈服强度、抗拉强度、加工硬化指数和塑性应变比厚向各向异性降低,塑性应变比平面各向异性增大;板材的组织、力学性能和成形性能未获得有效改善和提高.
参考文献
[1] | 王孟君;黄电源;姜海涛.汽车用铝合金的研究进展[J].金属热处理,2006(9):34-38. |
[2] | Y. S. Liu;S. B. Kang;H. S. Ko.Texture and plastic anisotropy of Al-Mg-0.3Cu-1.0Zn alloys[J].Scripta materialia,19974(4):411-417. |
[3] | Y.J. Li;W.Z. Zhang;K. Marthinsen.Precipitation crystallography of plate-shaped Al_6(Mn,Fe) dispersoids in AA5182 alloy[J].Acta materialia,201217(17):5963-5974. |
[4] | Wei Wen;J.G. Morris.The effect of cold rolling and annealing on the serrated yielding phenomenon of AA5182 aluminum alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20041/2(1/2):204-216. |
[5] | 王孟君;黄电源;姜海涛;任杰.退火对汽车用5182铝合金板材组织与性能的影响[J].金属热处理,2007(9):18-20. |
[6] | 高家诚;陈志强;明文良.中间退火工艺对5182铝合金带材性能的影响[J].材料热处理学报,2009(3):146-149. |
[7] | W. C. Liu;J. G. Morris.Effect of pre-treatment on recrystallization and recrystallization textures of cold rolled CC AA 5182 aluminum alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20031/2(1/2):253-262. |
[8] | 舒龙卫;毛卫民;冯惠平;余永宁;徐进.冷轧低压电子铝箔退火加热过程中的再结晶和晶粒长大[J].中国有色金属学报,2002(z1):178-182. |
[9] | Nicolas Moulin;Estelle Parra-Denis;Dominique Jeulin;Christophe Ducottet;Annabelle Bigot;Elodie Boller;Eric Maire;Cecile Barat;Helmut Klocker.Constituent Particle Break-Up During Hot Rolling of AA 5182[J].Advanced Engineering Materials,20101/2(1/2):20-29. |
[10] | D. J. Lloyd;S. A. Court.Influence of grain size on tensile properties of Al-Mg alloys[J].Materials Science and Technology: MST: A publication of the Institute of Metals,200310(10):1349-1354. |
[11] | Shi-Hoon Choi;Jae-KwonChoi;Hyoung-Wook Kim;Seok-Bong Kang.Effect of reduction ratio on annealing texture and r-value directionality for acold-rolled A1-5% Mg alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20091/2(1/2):77-87. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%