对氧化物弥散强化MGH956冷轧板材再结晶退火后可形成较为均匀细小和极其粗大两种完全不同晶粒组织状态的再结晶行为进行了研究.采用光学显微镜对冷轧板材在700～ 1350.C,1～120min等温退火后的组织检验结果显示:这两种晶粒组织状态的再结晶在起始和完成温度、起始形核位置、及长大速率等方面均存在显著差异,表明MGH956冷轧板材的再结晶并非仅以一种,至少可以两种不同的机制形成,并且,这两种机制还可共同发生在同一板材,导致MGH956板材再结晶组织形貌呈多样性,晶粒尺寸出现极为明显的差异.
参考文献
| [1] | 田耘,李帅华,杨峥,柳光祖,雷喆.氧化物弥散强化MGH956合金板材的拉伸和持久性能[J].材料热处理学报,2013(z1):114-121. |
| [2] | NUTTING J;UBHI S;HUGHES TA.The development of microstructure in Incoloy MA 956[A].New York:IncoMap,1981:33-40. |
| [3] | R.C.KEUG;G.KRAUSS .Recrystallization in Oxide-Dispersion Strengthened Mechanically Alloyed Sheet Steel[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1996(7):1945-1960. |
| [4] | 田耘;李帅华;杨峥 等.氧化物弥散强化MGH956合金板材再结晶典型组织[J].钢铁研究学报,2011,23(增刊2):526-529. |
| [5] | BHADESHIA H K D H .Recrystallization of practical mechanically alloyed iron-base and nickel-base superalloy[J].Materials Science and Engineering (A),1997,223:64-77. |
| [6] | CHOU T S .Recrystallization behaviour and grain structure in mechanically alloyed oxide-dispersion strengthened mechanically alloyed steel[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,1997,223:78-90. |
| [7] | Capdevila C.;Jelenak H.;Bhadeshia HKDH.;Miller U. .Strain heterogeneity and the production of coarse grains in mechanically alloyed iron-based PM2000 alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):161-165. |
| [8] | CAPDEVILA C;CHENY L;LASSENN C K;et el .Hererogeneous deformation and recrystallization of iron-base oxide-dispersion strengthened PM2000 alloy[J].Materials Science and Technology,2001,17:693-699. |
| [9] | CHEN Y L;JONES A R .The microstructure and recrystallization of flow-formed oxide-dispersion-strengthened ferritic alloy:Part Ⅰ[J].Metallurgical and Materials Transactions (A),2002,33:3777-3785. |
| [10] | CHEN Y L;JONES A R;POND R C et al.The microstructure and recrystallization of flow-formed oxide-dispersion-strengthened ferritic alloy:Part Ⅱ[J].Metallurgical and Materials Transactions (A),2002,33:3787-3794. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%