采用Gleebe-1500D热压缩模拟试验机在变形温度350 ～500℃、应变速率0.001～ 5s-1的条件下对Al-17.5Si-4Cu-0.5Mg合金进行热压缩实验,研究该合金在热塑性变形下的流变应力行为及其热加工特性,研究结果表明:Al-17.5Si-4Cu-0.5Mg合金为正应变速率敏感材料;该合金可用Znenr-Hollomon参数双曲正弦形式来描述高温塑性变形时的流变应力行为;合金平均热变形激活能Q为308.61 kJ/mol.基于动态材料模型(DMM)建立了Al-17.5Si-4Cu-0.5Mg合金的热加工图,并结合热加工图和显微组织分析获得了该合金较优的热变形工艺参数:变形温度为400 ～470℃,应变速率为0.1s-1.
参考文献
| [1] | >Gupta;S.Ling .Microstructure and mechanical properties of hypo/hyper-eutectic Al-Si alloys synthesized using a near-net shape forming technique[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,1999(1/2):284-294. |
| [2] | ZHANGH H;DUAN H L;SHAO G J et al.Microstructure and mechanical properties of hypereutectic Al-Si alloy modified with Cu-P[J].RARE METALS,2008,27:59-63. |
| [3] | YEH J;TSAU C .A study of the microstructures and propertiesof an A390 aluminum alloy produced by the layer depositionprocess[J].Materials Science and Engineering A,1993,165(2):157-165. |
| [4] | KAPRANOS P .Thixoforming of an automotive part in A390 hypereutectic Al-Si alloy[J].Journal of Materials Processing Technology,2002,135:271-277. |
| [5] | L. Lasa;J. M. Rodriguez-Ibabe .Effect of composition and processing route on the wear behaviour of Al-Si alloys[J].Scripta materialia,2002(6):477-481. |
| [6] | OSORIO W R;GOULART P R;GARCIA A .Effect of silicon content on microstructure and electrochemical behavior of hypereutectic Al-Si alloys[J].Materials Letters,2008,62(3):365-369. |
| [7] | 王杰芳,谢敬佩,刘忠侠,李继文,翁永刚,王明星.国内外铝硅活塞合金的研究及应用述评[J].铸造,2005(01):24-27. |
| [8] | 陆文华;李盛隆;黄良余.铸造合金及其熔炼[M].北京:机械工业出版社,2002:262-339. |
| [9] | YI H K;ZHANG D;FAN T X et al.Microstructure of worn surface and wear debris of as-cast Al-17Si-xLa alloys under unlubricated conditions[J].Transactions of Nonferrous Metals Society of China,2013,13(3):564-567. |
| [10] | 万里,罗吉荣,兰国栋,梁琼华.挤压铸造过共晶A390合金的组织与力学性能[J].华中科技大学学报（自然科学版）,2008(08):92-95. |
| [11] | He Kezhun,Yu Fuxiao,Zhao Dazhi,Zuo Liang.Microstructural evolution of direct chill cast Al-15.5Si-4Cu-1Mg-1Ni-0.5Cr alloy during solution treatment[J].中国铸造,2011(03):264-268. |
| [12] | ZHAN X;ZHANG Z F;XU J .Effect of solution treatment on the microstructure and mechanical properties of AI-16.9Si-4.5Cu-0.15Mg Alloy[J].RARE METAL MATERIALS AND ENGINEERING,2011,40(Suppl):73-77. |
| [13] | 党小荔,杨伏良.Al-1.03Mg-1.00Si-0.04Cu铝合金热压缩变形及其加工图[J].中南大学学报（自然科学版）,2012(11):4234-4241. |
| [14] | S.Ramanathan,R.Karthikeyan,V.Deepak Kumar,G.Ganesan.Hot Deformation Behavior of 2124 Al Alloy[J].材料科学技术学报(英文版),2006(05):611-615. |
| [15] | 李成侣,潘清林,刘晓艳,何运斌,李文斌.2124铝合金的热压缩变形和加工图[J].材料工程,2010(04):10-14. |
| [16] | 张辉,伍豪杰,蒋福林.4045铝合金热变形行为及其加工图[J].湖南大学学报（自然科学版）,2013(08):83-89. |
| [17] | 张伟,杨伏良,甘卫平,欧定斌.Al-35Si高硅铝合金热变形行为的研究[J].材料导报,2005(10):136-138. |
| [18] | SHEPPARD T;PARSON N C;ZAIDI M A et al.Dynamic recrystallization in Al-Mg[J].Metal Science Journal,1983,17(10):481-487. |
| [19] | SELLARS C M;TEGART W J .Relationship between strength and structure in deformation at elevated temperatures[J].Mem Sci Rev Met,1966,63(9):731-745. |
| [20] | SELLARS C M;TEGART W J .On the mechanism of hot deformation[J].ACTA METALLURGICA,1966,14(9):1136-1138. |
| [21] | MENG G;LI B;LI H M et al.Hot deformation and processing maps of an Al-5.7wt.％ Mg alloy with erbium[J].Materials Science and Engineering A,2009,517:132-137. |
| [22] | Prasad YVRK;Rao KP .Processing maps and rate controlling mechanisms of hot deformation of electrolytic tough pitch copper in the temperature range 300-950 degrees C[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):141-150. |
| [23] | 祖利国,张晓泳,李超,周科朝,唐仁波.Ti-5Al-5Mo-5V-1Cr-1Fe合金热加工图及其组织演变[J].中南大学学报（自然科学版）,2012(08):2943-2950. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%