通过不同应力状态下热空气老化试验和高低温循环老化试验,研究了NR1151天然橡胶性能的老化变化情况.结果表明:在70,90℃和110℃不同温度下连续热空气老化时,NR1151天然橡胶材料的拉伸强度和拉断伸长率均随着老化时间增加而明显下降,温度越高则下降越快;90℃时,应力对NR1151的老化有明显的加速作用;高低温循环老化时,NR1151天然橡胶材料的拉伸性能老化速率变慢,且循环周期越短,性能老化速率越慢.
参考文献
| [1] | 雷卫华;王建华;田野.MVQ-EPDM并用胶及泡沫的热老化性能研究[J].特种橡胶制品,2005(3):16-18. |
| [2] | Brown RP.;Soulagnet G..Microhardness profiles on aged rubber compounds[J].Polymer Testing,20013(3):295-303. |
| [3] | Gillen, KT;Bernstein, R;Derzon, DK.Evidence of non-Arrhenius behaviour from laboratory aging and 24-year field aging of polychloroprene rubber materials[J].Polymer Degradation and Stability,20051(1):57-67. |
| [4] | Mogon Patel;Anthony R. Skinner;Amiya Chaudhry;Norman C. Billingham;Bernard Mahieu.Impact of thermal ageing on the tin catalyst species in room temperature vulcanised polysiloxane rubbers[J].Polymer Degradation and Stability,20041(1):157-161. |
| [5] | Chou HW;Huang JS;Lin ST.Effects of thermal aging on fatigue of carbon black-reinforced EPDM rubber[J].Journal of Applied Polymer Science,20072(2):1244-1251. |
| [6] | 赵泉林;李晓刚;高瑾.三元乙丙橡胶的人工气候老化[J].北京科技大学学报,2008(12):1422-1427. |
| [7] | 朱立群;黄慧洁;赵波.丁腈橡胶硫化胶在乙二醇中的加速老化失效及寿命预测[J].航空材料学报,2007(3):69-73. |
| [8] | Garbarczyk M.;Kuhn W.;Klinowski J.;Jurga S..Characterization of aged nitrile rubber elastomers by NMR spectroscopy and microimaging[J].Polymer: The International Journal for the Science and Technology of Polymers,200211(11):3169-3172. |
| [9] | 肖琰;魏伯荣.天然橡胶硫化胶的热氧老化性研究[J].合成材料老化与应用,2006(2):21-23,54. |
| [10] | 张福全;陈美;王永周;廖建和.天然橡胶的老化特征及防护技术[J].特种橡胶制品,2011(3):57-60. |
| [11] | 夏洪花;王新坤;吴灿伟.橡胶材料的老化及寿命预测方法研究[J].航空材料学报,2011(z1):219-222. |
| [12] | 曹翠微;肖琰;魏伯荣.动态热机械法研究天然橡胶硫化胶的热氧老化性能[J].宇航材料工艺,2006(4):58-60. |
| [13] | 胡文军;刘占芳;陈勇梅.橡胶的热氧加速老化试验及寿命预测方法[J].橡胶工业,2004(10):620-624. |
| [14] | 王作龄.防老剂应用技术[J].世界橡胶工业,2001(01):55-59. |
| [15] | 王思静;熊金平;左禹.橡胶老化机理与研究方法进展[J].合成材料老化与应用,2009(2):23-33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%