采用电化学辅助沉积方法对AZ31B镁合金进行硅烷化处理,借助于动电位极化曲线和电化学阻抗谱等电化学测试手段研究了γ-(甲基丙烯酰氧基)丙基三甲氧基硅烷(KH-570)添加量对膜层质量及耐蚀性能的影响,并比较了利用羟基磷灰石(HA)颗粒、铈盐离子(Ce3+)两种改性物质改良硅烷溶液后所制得膜层的质量及耐蚀性能.结果表明:AZ31B镁合金经电化学辅助沉积硅烷处理后,表面生成一层均匀而致密的硅烷透明膜层,有效地减缓了镁合金的腐蚀行为,促使其自腐蚀电流密度大大降低;在硅烷电化学辅助沉积处理过程中,KH-570存在最佳添加量,当其添加体积约为8 mL时所制备出的硅烷膜层质量最好、耐蚀性能最佳;通过改良硅烷溶液,电化学辅助沉积制备的硅烷膜层质量进一步提高,Ce3+改良效果更佳.
参考文献
| [1] | Ng, W.F.;Chiu, K.Y.;Cheng, F.T..Effect of pH on the in vitro corrosion rate of magnesium degradable implant material[J].Materials science & engineering, C. Biomimetic and supramolecular systems,20106(6):898-903. |
| [2] | Staiger MP;Pietak AM;Huadmai J;Dias G.Magnesium and its alloys as orthopedic biomaterials: A review[J].Biomaterials,20069(9):1728-1734. |
| [3] | Liu,X.;Yue,Z.;Romeo,T.;Weber,J.;Scheuermann,T.;Moulton,S.;Wallace,G..Biofunctionalized anti-corrosive silane coatings for magnesium alloys[J].Acta biomaterialia,201310(10):8671-8677. |
| [4] | 徐以兵 .铝合金和镁合金的表面硅烷化处理研究[D].湖南大学,2008. |
| [5] | 韩利华;马庆国;冯晓健;康举.镀锌层表面KH-560硅烷膜耐蚀性能研究[J].材料工程,2010(6):45-49. |
| [6] | 杨玉昌;王锋;胡剑青;涂伟萍.冷轧钢表面锆盐复合硅烷涂层的性能及结构研究[J].材料工程,2013(4):50-55,62. |
| [7] | 乔丽英;何聪;谈安强;况新亮;高家诚.硅烷化处理在镁合金表面防腐中的应用[J].功能材料,2013(9):1217-1220,1225. |
| [8] | W. J. van Ooij;D. Zhu;M. Stacy;A. Seth;T. Mugada;J. Gandhi;P. Puomi.Corrosion Protection Properties of Organofunctional Silanes-An Overview[J].清华大学学报（英文版）,2005(06):639-664. |
| [9] | 张津;吴超云;黄福祥;张微.AZ31B镁合金表面硅烷处理研究[J].中国腐蚀与防护学报,2008(3):146-150. |
| [10] | Zomorodian, A.;Brusciotti, F.;Fernandes, A.;Carmezim, M.J.;Moura e Silva, T.;Fernandes, J.C.S.;Montemor, M.F..Anti-corrosion performance of a new silane coating for corrosion protection of AZ31 magnesium alloy in Hank's solution[J].Surface & Coatings Technology,201221(21):4368-4375. |
| [11] | Muqin Li;Jiang Liu;Jungang Li;Yongjiang Li;Shouduo Lu;Yuqi Yuan.The enhanced corrosion resistance of UMAO coatings on Mg by silane treatment[J].自然科学进展（英文版）,2014(5):486-491. |
| [12] | Montemor MF;Ferreira MGS.Analytical and microscopic characterisation of modified bis-[triethoxysilylpropyl] tetrasulphide silane films on magnesium AZ31 substrates[J].Progress in Organic Coatings: An International Review Journal,20073(3):228-237. |
| [13] | 胡吉明;杨亚琴;张鉴清;曹楚南.电沉积防护性硅烷薄膜的研究现状与展望[J].中国腐蚀与防护学报,2011(1):1-9. |
| [14] | 胡吉明;刘倞;张鉴清;曹楚南.LY12铝合金表面电化学沉积制备DTMS硅烷膜及其耐蚀性研究[J].高等学校化学学报,2006(6):1121-1125. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%