对铸造Ti-47.5Al-2.5V-1.0Cr-0.2Zr(原子分数/％)合金层片组织进行了疲劳测试,获得了单一应力下的疲劳寿命数据,通过断口观察和数据统计处理,分析了疲劳寿命的分布特点及其控制因素.结果表明:实验合金的疲劳寿命具有显著波动,波动范围为103～ 106周;并集中分布在长、短两个寿命区间内.这一现象和导致疲劳试样失效的疲劳裂纹源的类型有关;其中,短寿命试样的疲劳裂纹起源于疏松孔洞,长寿命试样的疲劳裂纹源为弥合界面和软取向层片界面.建立了三种裂纹源对疲劳寿命的影响的两参数威布尔分布模型,可进行对应于某一失效概率的疲劳寿命预测.三种疲劳裂纹源中,疏松孔洞对疲劳寿命不利影响的程度最为严重.
参考文献
| [1] | Young-Won Kim.Gamma Titanium Aluminides: Their Status and Future[J].JOM,19957(7):39-41. |
| [2] | S. K. Jha;J. M. Larsen;A. H. Rosenberger.The role of competing mechanisms in the fatigue life variability of a nearly fully-lamellar gamma-TiAl based alloy[J].Acta materialia,20055(5):1293-1304. |
| [3] | S.K. Jha;J.M. Larsen;A.H. Rosenberger.The Role of Competing Mechanisms in the Fatigue-Life Variability of a Titanium and Gamma-TiAl Alloy[J].JOM,20059(9):50-54. |
| [4] | Trail SJ.;Bowen P..EFFECTS OF STRESS CONCENTRATIONS ON THE FATIGUE LIFE OF A GAMMA-BASED TITANIUM ALUMINIDE[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,19950(0):427-434. |
| [5] | 张继;仲增镛.TiAl金属间化合物工程实用化研究与进展[J].中国材料进展,2010(2):9-13. |
| [6] | 张继.铸造钛铝合金组织与力学性能[J].航空材料学报,1998(03):29. |
| [7] | 万文娟;韩波;韩伟;张继.TiAl 合金择优取向层片组织的高周疲劳行为[J].航空材料学报,2016(1):87-92. |
| [8] | Bowen P.;James AW.;Chave RA..CYCLIC CRACK GROWTH IN TITANIUM ALUMINIDES[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,19950(0):443-456. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%