研究表面涂覆有机硅涂层的聚碳酸酯( Polycarbonate, PC)透明件在乙醇中的溶剂-应力开裂( Environ-mental stress cracking, ESC)行为,利用自制的环境力学测试装置考察PC/涂层体系在溶剂与应力共同作用下的应力松弛行为和表面裂纹形貌。结果表明：有机硅涂层在一定程度上改善了透明件的耐溶剂-应力开裂性能,带涂层试样在乙醇环境中的应力松弛比纯PC明显减慢,并且表面裂纹数量减少；有机硅涂层对乙醇与试样表面层的接触及扩散吸收起到有效阻隔,进而可降低溶剂对 PC 的塑化作用；涂层与 PC 基体力学性质较为匹配,在承载条件下涂层不易发生脱落开裂,在溶剂-应力共同作用过程中仍然能对 PC基体起到一定保护作用。
Environmental stress cracking( ESC) behavior of silicone coated polycarbonate ( PC) in ethanol was studied. Stress relaxa-tion of PC and PC/silicone coating under a combined action of ethanol and stress was measured by self-made three point bending equip-ment. After stress relaxation testing, crack morphology was observed by polarizing microscope. The results indicate that silicone coating is able to improve the stress cracking resistance of PC parts in ethanol. The coated PC shows slower stress relaxation rate and less num-ber of cracks than pristine PC. It is mainly attributed to that the silicone coating can provide barrier effect to the absorption and diffu-sion of ethanol in PC substrate. Furthermore, the mechanical properties of flexible silicone coating matched fairly well with that of PC, so that the coating is uneasy to peel off from PC substrate during the ESC testing. The silicone coating has a favorable effect to protect PC substrate from ESC under the combined action of solvent and stress.
参考文献
| [1] | Delpech MC.;Coutinho FMB.;Habibe MES..Bisphenol A-based polycarbonates: characterization of commercial samples[J].Polymer Testing,20022(2):155-161. |
| [2] | Lloyd M. Robeson.Environmental Stress Cracking: A Review[J].Polymer engineering and science,20133(3):453-467. |
| [3] | Chen, Y.;Nie, X.;Zhou, S.;Zou, H.;Liang, M.;Liu, P..Investigations of environmental stress cracking resistance of HDPE/UHMWPE and LDPE/UHMWPE blends[J].Journal of Polymer Research,20135(5):141-1-141-7. |
| [4] | Lin, L.;Schlarb, A.K..A study on environmental stress cracking in nano-SiO _-filled polycarbonate[J].Journal of Materials Science,201218(18):6614-6620. |
| [5] | 张旋;钟艳莉;颜悦;厉蕾.聚碳酸酯透明材料表面耐磨涂层的纳米力学性能和耐磨性研究[J].材料工程,2014(1):79-84. |
| [6] | 刘仲阳;陈子辉;李晓宁.聚碳酸酯表面有机硅耐磨加硬涂层的增韧研究[J].有机硅材料,2015(3):179-184. |
| [7] | Krystelle Lionti;Berangere Toury;Cedric Boissiere.Hybrid silica coatings on polycarbonate: enhanced properties[J].Journal of Sol-Gel Science and Technology,20131(1):52-60. |
| [8] | 彭叔森;曾志翔;韩金;陈建敏;乌学东.有机硅溶胶-凝胶防腐蚀涂层研究进展[J].中国材料进展,2014(2):77-85. |
| [9] | Briscoe BJ.;Pelillo E.;Fiori L..Nano-indentation of polymeric surfaces[J].Journal of Physics, D. Applied Physics: A Europhysics Journal,199819(19):2395-2405. |
| [10] | Sousa AR;Amorim KLE;Medeiros ES;Melo TJA;Rabello MS.The combined effect of photodegradation and stress cracking in polystyrene[J].Polymer Degradation and Stability,20067(7):1504-1512. |
| [11] | Zhang, Xuan;Zhang, Xiaofeng;Yan, Yue;Zhong, Yanli;Li, Lei;Zhang, Guanli.Adhesion and thermal stability enhancement of IZO films by adding a primer layer on polycarbonate substrate[J].Physica status solidi, A. Applications and materials science ePSS,20154(4):831-839. |
| [12] | Lutfi F. Al-Saidi;Kell Mortensen;Kristoffer Almdal.Environmental stress cracking resistance. Behaviour of polycarbonate in different chemicals by determination of the time-dependence of stress at constant strains[J].Polymer Degradation and Stability,20033(3):451-461. |
| [13] | Turnbull A.;Pillai S.;Maxwell AS..Comparative assessment of slow strain rate, 4-pt bend and constant load test methods for measuring environment stress cracking of polymers[J].Polymer Testing,20002(2):117-129. |
| [14] | Raman A.;Farris RJ.;Lesser AJ..Effect of stress state and polymer morphology on environmental stress cracking in polycarbonate[J].Journal of Applied Polymer Science,20032(2):550-564. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%