采用喷射裂解法,以羰基铁为催化剂前驱体,吡啶为碳源,通过改变温度或比例(V(羰基铁)∶V(吡啶))制备了不同形貌的碳纳米材料.采用氯化铵热处理法去除碳材料中的铁催化剂,得到具有空心结构的碳纳米笼和石墨烯片层,采用高分辨透射电镜(HRTEM)对载体的形貌特征进行表征.然后将Pt纳米粒子沉积在碳载体上,得到不同的Pt/C催化剂.通过HRTEM、X射线衍射(XRD)和电化学测试对合成催化剂的结构、形貌和电化学性能进行了表征.实验结果表明:制备温度和反应物比例的变化导致产物的结构形貌发生变化;当作为催化剂载体时,其微观结构和石墨化程度对催化剂的催化活性和稳定性有很大的影响.
参考文献
| [1] | 衣宝廉.燃料电池--原理@技术@应用[M].北京:化学工业出版社,2003 |
| [2] | Knights S D et al.Aging mechanisms and lifetime of PEFC and DMFC[J].Journal of Power Sources,2004,127(1-2):127. |
| [3] | 尹鸽平,杜春雨,王振波.质子交换膜燃料电池催化剂稳定性研究进展（Ⅰ）[J].电源技术,2008(03):143-146. |
| [4] | Rao V et al.The influence of carbon support porosity on the activity of PtRu/Sibunit anode catalysts for methanol oxidation[J].Journal of Power Sources,2005,145(02):178. |
| [5] | Ralph T R;Hogarth M P .Catalysis for low temperature fuel cells[J].Platinum Metals Review,2002,46(01):3. |
| [6] | Cameron D S;Cooper S J et al.Carbons as supports for precious metal catalysts[J].Catalysis Today,1990,7(02):113. |
| [7] | 李旭光,邢巍,杨辉,陆天虹.活性炭载体对聚合物电解质膜燃料电池中炭载铂电催化剂性能的影响[J].分析化学,2002(07):788-791. |
| [8] | 张传香 .超级电容器NiO/介孔碳复合电极材料的制备及其性能研究[D].南京航空航天大学,2008. |
| [9] | 段力群,马青松,陈朝辉.聚硅氧烷制备高比表面积微介孔炭材料[J].新型炭材料,2013(03):235-240. |
| [10] | 朱舜,姚玉元,林启松,吕汪洋,陈文兴.介孔碳负载铂催化剂的制备及降解甲醛的研究[J].功能材料,2013(21):3190-3194,3198. |
| [11] | Liang C D;Li Z J;Dai S .Mesoporous crbon mterials:Synthesis and modification[J].ANGEWANDTE CHEMIE-INTERNATIONAL EDITION,2008,47(20):3696. |
| [12] | Yu Zhang;Hong-Bin Zhang;Guo-Dong Lin;Ping Chen;You-Zhu Yuan;K. R. Tsai .Preparation, Characterization and catalytic hydroformylation properties of carbon nanotubes-supported Rh-phosphine catalyst[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,1999(2):213-224. |
| [13] | Kim Junhyung et al.Pt-covered multiwall carbon nanotubes for oxygen reduction in fuel cell application[J].J Phys Chem Lett,2011,2(11):1332. |
| [14] | 吴燕妮,廖世军.以切短多壁碳纳米管为载体制备高活性Pt/SCNT及PtRu/SCNT燃料电池催化剂[J].物理化学学报,2010(03):669-674. |
| [15] | Rodriguez Nelly M;Kim Myung-soo;Terry R .Carbon nanofibers:A unique catalyst support medium[J].Journal of Physical Chemistry,1994,98(50):13108. |
| [16] | Joo S H;Park J Y;Tsung C K et al.Thermally stable Pt/mesoporous reactions[J].NATURE MATERIALS,2009,8:126. |
| [17] | 刘树和,英哲,王作明,李峰,白朔,闻雷,成会明.天然石墨球-热解炭核壳结构的制备及电化学性能研究[J].新型炭材料,2008(01):30-36. |
| [18] | 张永刚,王成扬,闫裴.石墨微粒的表面化学沉积包覆[J].新型炭材料,2010(03):211-217. |
| [19] | Wu, Z.;Lv, Y.;Xia, Y.;Webley, P.A.;Zhao, D. .Ordered mesoporous platinum@graphitic carbon embedded nanophase as a highly active, stable, and methanol-tolerant oxygen reduction electrocatalyst[J].Journal of the American Chemical Society,2012(4):2236-2245. |
| [20] | 李云霞,魏子栋,赵巧玲,丁炜,张骞,陈四国.石墨烯负载Pt催化剂的制备及催化氧还原性能[J].物理化学学报,2011(04):858-862. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%