混凝土结构决定其性能.通过扫描电镜和压汞试验,表征和分析了聚羧酸减水剂对混凝土硬化水泥浆体、界面结构和水泥石孔结构的影响.结果表明,早龄期的混凝土硬化水泥浆体和界面结构裂纹较宽,裂缝较多,而龄期长则结构较密实;相同龄期掺有聚羧酸减水剂的混凝土硬化水泥浆体和界面过渡区结构裂缝数量、裂纹宽度均小于萘系减水剂;聚羧酸减水剂降低了水泥石的平均孔径,最可几孔径和孔隙率;少害孔和无害孔的含量多,而有害孔和多害孔含量少.聚羧酸减水剂对混凝土结构的作用优于萘系减水剂.
参考文献
| [1] | S. Ng;J. Plank .Interaction mechanisms between Na montmorillonite clay and MPEG-based polycarboxylate superplasticizers[J].Cement and Concrete Research,2012(6):847-854. |
| [2] | J. Pickelmann;J. Plank .A mechanistic study explaining the synergistic viscosity increase obtained from polyethylene oxide (PEO) and β-naphthalene sulfonate (BNS) in shotcrete[J].Cement and Concrete Research,2012(11):1409-1416. |
| [3] | Serina Ng;Ezzeldin Metwalli;Peter Miiller-Buschbaum.Occurrence of intercalation of PCE superplasticizers in calcium aluminate cement under actual application conditions, as evidenced by SAXS analysis[J].Cement and Concrete Research,2013:191-198. |
| [4] | Kazuo Yamada .Basics of analytical methods used for the investigation of interaction mechanism between cements and superplasticizers[J].Cement and Concrete Research,2011(7):793-798. |
| [5] | Ammar Yahia .Shear-thickening behavior of high-performance cement grouts - Influencing mix-design parameters[J].Cement and Concrete Research,2011(3):230-235. |
| [6] | Prokopskl G;Halbiniak J .Interfacial transition zone in cementious materials[J].Cement and Concrete Research,2000,30(04):579. |
| [7] | Azimah Hussin;Colin Poole .Petrography evidence of the interfacial transition zone (ITZ) in the normal strength concrete containing granitic and limestone aggregates[J].Construction and Building Materials,2011(5):2298-2303. |
| [8] | Cwirzen A;Pentrala V .Aggregate-cement paste transition zone properties affecting the salt-frost damage of high-performance concrete[J].Cement and Concrete Research,2005,35(05):671. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%