通过DTA研究了TeO2-PbO-B2O3-Bi2O3-Li2O系统玻璃中TeO2、PbO物质的量比变化对玻璃转变温度(Tg)的影响,重点研究了n(TeO2)∶n(PbO)=2∶1条件下Li2O含量对玻璃转变温度的影响,并采用IR和XRD对玻璃的结构和析晶性进行了分析.结果表明:随着Li2O含量(2.7%~6.6%,摩尔分数)的增加,Tg呈N型变化趋势,当Li2O为2.7%(摩尔分数)时,Tg为最低值(300℃).碲系统玻璃中形成了[TeO]三角双锥体结构,它与[BO4]、BiO6]等多面体共同构成了玻璃的三维网络结构,该玻璃经热处理后易形成Bi2 TeO5晶体而会影响Tg.
参考文献
[1] | Kyoung-Kook Hong;Joo-Youl Huh .Role of PbO-Based Glass Frit in Ag Thick-Film Contact Formation for Crystalline Si Solar Cells[J].Metals and Materials International,2009(2):307-312. |
[2] | Kim B S;Lim E S;Lee J H et al.Effect of Bi2O3 content on sintering and crystallization behavior of low-temperature firing Bi2 O3-B2 O3-SiO2 glasses[J].Journal of the European Ceramic Society,2007,27(2-3):819. |
[3] | Alan F C;Kenneth W H;Brian J L et al.Thick-film pastes containing lead-tellurium-boron-oxides,and their use in the manufacture of semiconductor devices[P].US,A1,0232746,2011-05-04. |
[4] | 西北轻工学院.玻璃工艺学[M].北京:中国轻工业出版社,1982 |
[5] | Marek N;Wlodzimierz M;Jerzy J et al.Structure and op tical properties of glasses from Li2O-Bi2O3-PbO system[J].JOURNAL OF MOLECULAR STRUCTURE,2005,744-747(03):604. |
[6] | Doweidar, H.;El-Damrawi, G.;Mansour, E.;Fetouh, R.E. .Structural role of MgO and PbO in MgO-PbO-B_2O_3 glasses as revealed by FTIR; A new approach[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2012(5):941-946. |
[7] | Zhou Yongtao;Yang Yunxia;Huang Feihong et al.Characterization of new tellurite glasses and crystalline phases in the TeO2-PbO-Bi2 O3-B2 O3 system[J].JOURNAL OF NON-CRYSTALLINE SOLIDS,2014,386:92. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%