用氧乙炔火焰喷涂在Q235钢表面制备粉煤灰复合涂层.采用SEM和XRD分析了涂层的界面形貌和物相组成,并测试了粉煤灰复合涂层的耐蚀性和耐磨粒磨损性能.结果表明,涂层表面致密,结合性良好,且有3Al2O3·2SiO2、Ca2SiO4、TiB2等新相产生;涂层具有良好的耐酸性和耐磨性,其耐酸性、耐磨粒磨损性分别比基体提高了11.8倍、7.67倍.
参考文献
| [1] | 姚志通 .固体废弃物粉煤灰的资源化利用[D].杭州:浙江大学,2010. |
| [2] | 吴元锋,仪桂云,刘全润,李风海,赵丽伟,马名杰.粉煤灰综合利用现状[J].洁净煤技术,2013(06):100-104. |
| [3] | 马壮,陶莹,李智超.热化学反应法制备粉煤灰陶瓷涂层展望[J].硅酸盐通报,2012(06):1514-1517,1522. |
| [4] | L. Rama Krishna;D. Sen;D. Srinivasa Rao;G. Sundararajan .Coatability and characterization of fly ash deposited on mild steel by detonation spraying[J].Journal of Thermal Spray Technology,2003(1):77-79. |
| [5] | MishraSC;MishraPC;RoutbKC.Fly ash as a coating material for plasma spray coatings[A].Jamshedpur:National Institute of Technology,1999 |
| [6] | Mishra S C;Routb K C;Padmanabhanc P V A et al.Plasma spray coating of fly ash pre-mixed with lumimum powder deposited on metal substrates[J].J Mater Process Techn,2000,102:9. |
| [7] | Alok Satapathy;Suvendu Prasad Sahu;Debadutta Mishra.Plasma spray deposition of fly ash+aluminum coatings on steel substrates[A].Hamirpur:National Institute of Technology,2009 |
| [8] | 马壮,陶莹,闫翠娟,李智超.粉煤灰复合涂层腐蚀磨损性能研究[J].材料导报,2013(16):127-130. |
| [9] | Al2O3对硅酸盐矿物涂层耐蚀性能的影响[J].热加工工艺,2012(22):169-171. |
| [10] | 马壮,陶莹,闫翠娟,李智超.Al-TiO2-B2O3系粉煤灰复合涂层冲蚀磨损性能研究[J].硅酸盐通报,2013(09):1747-1750. |
| [11] | 马壮,李剑,闫翠娟,李智超.粉煤灰玻璃/陶瓷复合涂层冲蚀磨损性能研究[J].硅酸盐通报,2013(08):1684-1687. |
| [12] | 马壮,李剑,闫翠娟,李智超.粉煤灰玻璃/陶瓷复合涂层制备工艺及性能研究[J].硅酸盐通报,2013(04):699-703. |
| [13] | 马壮,杨杰,韩子钰,羊娟,孙方红.热反应法制备粉煤灰陶瓷涂层中的CeO2对涂层耐磨性能的影响[J].材料保护,2013(09):54-56. |
| [14] | 马壮,林鹏,董世知,李智超.在AZ91D表面SHS反应热喷涂Al-CuO系Al2O3基复相陶瓷涂层[J].中国有色金属学报,2009(08):1379-1384. |
| [15] | 陈燕,芦笙,陈静,段珍珍.AZ91D镁合金等离子喷涂Ni-Al/陶瓷涂层的组织和性能[J].中国有色金属学报,2012(04):1094-1101. |
| [16] | 王孝建,王银军.超音速火焰喷涂WC-12Co涂层抗磨粒磨损性能研究[J].热喷涂技术,2010(03):44-48. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%