以NaVO3、Zn(NC3)2·6H2O为原料,采用水热法合成了铕离子掺杂Zn2 (OH)3 VO3纳米晶体.运用X射线粉末衍射、扫描电子显微镜、荧光测试仪对纳米晶进行了表征,研究了水乙醇体系不同pH值对产物晶相、微观形貌及荧光性能的影响.在溶剂体系pH值为7~10时,得到片状的Zn2 (OH)3 VO3,而在pH值为4~6和11~12时得到Zn3 (OH)2V2O7·2H2O,表明强酸性和强碱性的溶剂体系都不太适合Zn2 (OH)3 VO3的合成,而最佳的合成体系为中性偏碱性;荧光测试表明在pH=10的水乙醇体系下合成的Zn2(OH)3VO3∶8%Eu3+纳米片的荧光性能最好,其中发射主峰位于612 nm处.

参考文献

[1] Burland D;Miller R;Walsh C .Second-order nonlinearity in poled-polymer systems[J].CHEMICAL REVIEWS,1994,94(1)
[2] Beecroft L;Ober C .Nanocomposite materials for optical applications[J].CHEMISTRY OF MATERIALS,1997,9:1302.
[3] Zhang L;Chen D;Jiao X .Monoclinic structured BiVO4 nanosheets:Hydrothermal preparation,formation mechanism,and coloristic and photocatalyticproperties[J].Journal of Physical Chemistry B,2006,110:2668.
[4] Zhang S Y;Ci L J;Liu H .Synthesis characterization and electrochemical properties of Cu3 V2 O7 (OH)2 @ 2H2O nano-structures[J].J Phys Chem C,2009,113:8624.
[5] 王莉丽;刘连利;吕红艳 等.LaYO4:Eu3+水热制备及荧光性能研究[J].材料导报:研究篇,2014,28(6):14.
[6] 许静,傅亚,原金海,刘德蓉,田敉,王月.Ba_3V_2O_8∶Eu~(3+)纳米花的制备及光致发光性能研究[J].功能材料,2012(18):2564-2567.
[7] 马华,冀伟强,杨晓婧,陶占良,陈军.CoV2O6纳米线/微米棒的制备及其在锂离子电池中的应用[J].中国科学B辑,2009(09):918-925.
[8] 王雅静,杨义洪,肖林久,谢颖,刘娇娜,刘钢.Er3+掺杂GdVO4纳米粒子的制备及发光性能研究[J].化工新型材料,2014(11):117-119,122.
[9] 陈青,孙嬿,段小川,郑文君.单斜BiV04的离子液体辅助水热合成及表征[J].高等学校化学学报,2011(03):667-672.
[10] Wang M;Shi Y J;Jiang G Q .3D hierarchical Zn3-(OH)2V2O7 @ 2H2O and Zn3 (VO4)2 microspheres:Synthesis,characterization and photoluminescence[J].Materials Research Bulletin,2012,47:18.
[11] Shi R;Wang Y J;Zhou F et al.Zn3(OH)2V2O7 @ 2H2O and Zn3 V2 O8 nanostructures:Controlled fabrication and photocatalytic performance[J].Journal of Materials Chemistry,2011,21:6313.
[12] Guo H X;Di G;Zheng Z S et al.Hydrothermal synthesis and visible light photocatalytic activities of Zn3 (VO4)2 nano-rods[J].Journal of Materials Research,2014,29(24):2934.
[13] 蒋亚琪,贺淳晓,贾艳艳,谢兆雄.过渡金属离子掺杂Zn3(OH)2V2O7·2H2O的合成及其光催化性质[J].无机化学学报,2012(10):2170-2178.
[14] Zhang S Y;Lei N;Ma W Q et al.Fabrication of ultralong Zn3 (OH)2V2O7 @ 2H2O nanobelts and its application in lithium-ion batteries[J].Materials Letters,2014,129:91.
[15] Xueyan Wu;Hongpeng You;Hongtao Cui .Vacuum ultraviolet optical properties of (La, Gd)PO_4:RE~3+(RE=Eu, Tb)[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2002(9):1531-1538.
[16] Wang YH;Guo X;Endo T;Murakami Y;Ushirozawa M .Identification of charge transfer (CT) transition in (Gd,Y)BO3 : Eu phosphor under 100-300nm[J].International Journal of Quantum Chemistry,2004(7):2242-2248.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%