采用静电纺丝技术制备聚乙烯醇/海藻酸钠复合纳米纤维膜，利用氯化钙乙醇溶液进行交联改性。研究复合纳米纤维制备、交联工艺对材料表面形貌、耐水性、热性能等的影响。结果表明：纳米纤维直径在200~500 nm之间，纤维平均直径随海藻酸钠含量的增大而增大，复合纳米纤维结晶度随海藻酸钠含量的增大而降低，热稳定性随海藻酸钠含量的增大而下降。交联改性后复合纳米纤维材料耐水性提高，纤维形貌保持，纤维之间粘结增多，材料不发生熔融相转变，热稳定性下降。
Poly(vinyl alcohol)/sodium alginate composite nanofiber membranes were prepared through electro-spinning and were crosslinked through calcium chloride ethanol solution.Surface morphology and water resistance as well as thermal behavior of the nanofiber membrane before and after crosslinked were investigated.The results indica-ted that nanofiber have diameter of 200 - 500 nm and average diameter of composite nanofiber membrane increased with the content of sodium alginate increasing.Crystallinity and decomposition temperature of composite nanofiber membrane decreased with the content of sodium alginate increasing.Water resistance of nanofiber improved after the nanofiber was crosslinked.Surface morphology of fiber remains unchanged and sticky between fibers increased after the nanofiber was crosslinked.Molten phase transition disappeared and decomposition temperture of composite nanofi-ber membrane decreased after the nanofiber was crosslinked.
参考文献
| [1] | FANG Jian;NIU HaiTao;LIN Tong;WANG XunGai.Applications of electrospun nanofibers[J].科学通报（英文版）,2008(15):2265-2286. |
| [2] | Huarong Nie;Aihua He;Jianfen Zheng.Effects of Chain Conformation and Entanglement on the Electrospinning of Pure Alginate[J].Biomacromolecules,20085(5):1362-1365. |
| [3] | 樊亚男;蔡志江;赵孔银.静电纺丝制备海藻酸钠基复合纳米纤维的研究进展[J].高分子通报,2013(11):70-75. |
| [4] | K Tarun;N Gobi.Calcium alginate/PVA blended nano fibre matrix for wound dressing[J].Indian journal of fibre & textile research,20122(2):127-132. |
| [5] | 张学良;岑桂秋;牛迪;李嘉诚;林强.添加不同物质的聚乙烯醇/海藻酸钠静电纺丝研究[J].合成纤维,2012(3):25-31. |
| [6] | 冯燕;孙润军;刘呈坤.海藻酸钠/聚乙烯醇/银复合纤维的静电纺丝[J].合成纤维,2011(12):13-17. |
| [7] | 李沉纹;管海燕;李卓恒;于彩平;罗明和;卢来春.静电纺丝技术制备载药聚乙烯醇-海藻酸钠纳米纤维[J].中国药学杂志,2013(12):980-985. |
| [8] | 谢红;卢华;黄华;卢来春;管海燕.载药聚乙烯醇/海藻酸钠静电纺丝纤维的改性及其药物体外释放研究[J].第三军医大学学报,2011(23):2485-2489. |
| [9] | Costa, R.G.F.;Ribeiro, C.;Mattoso, L.H.C..Study of the effect of rutile/anatase TiO_2 nanoparticles synthesized by hydrothermal route in electrospun PVA/TiO_2 nanocomposites[J].Journal of Applied Polymer Science,20136(6):4463-4469. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%