普通硅酸盐水泥在尾砂胶结充填中被广泛使用，但存在两个问题：水泥生产过程能耗高，需要大量不可再生资源、CO2排放量大；充填成本高，灰砂比可调范围窄，适应性差。为消除该影响，可采用工业副产品粒化高炉矿渣，辅以少量激发材料形成不同类型固化剂以取代水泥固化尾砂。该类固化剂水化所需碱度低，形成的水化硅酸钙在钙硅比上比普通硅酸盐水泥低，因而其强度和稳定性优异，同时可形成水滑石等产物填充结构孔隙；此外，还能因地制宜调整固化剂配方，固化剂性价比高，可在满足充填需求的同时提高对尾砂的适应性和固化效率。
Ordinary Portland cement (OPC)has been widely used for cemented filling of tailing,while there are two main problems:high energy and non-renewable resources consumption,and high CO2 emission during cement pro-duction;high filling cost,small tolerable range of binder/tailing ratio,and poor adaptability for tailings.In order to mitigate the effect,the industrial by product — ground granulated blastfurnace slag (GGBS)can be used as the major component to form the different stabilizers with a few activators,which may provide a replacement for Portland ce-ment in the tailing cemented area.The stabilizer requires lower alkaline environment,and the calcium silicate hydrates evolved from the stabilizer have lower Ca/Si ratio than that of Portland cement,and consequent higher strength and durability.Meanwhile,the stabilizer may form hydrotalcite that could fill the voids of the stabilized structure,and the compositions of stabilizer could be adj usted according to local conditions.Therefore the stabilizer is more cost-effec-tive,more adaptable for the tailings,and more efficient for the stabilization of tailings,while the filling demand could still be met.
参考文献
| [1] | D. Higgins.Briefing: GGBS and sustainability[J].Construction materials,20073(3):99-101. |
| [2] | 赵传卿;胡乃联.充填胶凝材料的发展与应用[J].黄金,2008(1):25-29. |
| [3] | 秦大健.新型尾砂胶结材料的实验研究[J].煤炭与化工,2014(9):49-51,56. |
| [4] | 程斌;刘东玲;陈能革;纪宪坤.铁尾矿全尾砂胶结充填技术及新型固化剂的应用[J].现代矿业,2013(11):158-160. |
| [5] | 纪宪坤;周永祥;杨建辉;邵正明;王明远.铁尾矿全尾砂胶结充填固化剂及工程应用[J].新型建筑材料,2014(4):30-33. |
| [6] | S. SONG;D. SOHN;H. M. JENNINGS.Hydration of alkali-activated ground granulated blast furnace slag[J].Journal of Materials Science,20001(1):249-257. |
| [7] | W.A.Tasong;S.Wild.Mechanisms by which ground granulated blastfurnace slag prevents sulphate attack of lime-stabilised kaolintie[J].Cement and Concrete Research,19997(7):975-982. |
| [8] | Puppala AJ;Intharasombat N;Vempati RK.Experimental studies on ettringite-induced heaving in soils[J].Journal of geotechnical and geoenvironmental engineering,20053(3):325-337. |
| [9] | Anand J. Puppala;Julie Ann Griffin;Laureano R. Hoyos;Suppakit Chomtid.Studies on Sulfate-Resistant Cement Stabilization Methods to Address Sulfate-Induced Soil Heave[J].Journal of geotechnical and geoenvironmental engineering,20044(4):391-402. |
| [10] | S.Wild;J.M.Kinuthia.Suppression of swelling associated with ettringite formation in lime stabilized sulphate bearing clay soils by partial substitution of lime with ground granulated blastfurnace slag[J].Engineering Geology,19994(4):257-277. |
| [11] | Vahid R. Ouhadi;Raymond N. Yong.Ettringite Formation And Behaviour In Clayey Soils[J].Applied clay science,20081/2(1/2):258-265. |
| [12] | Akino Tsujimura;Miho Uchida;Akitsugu Okuwaki.Synthesis and sulfate ion-exchange properties of a hydrotalcite-like compound intercalated by chloride ions[J].Journal of Hazardous Materials,20071/2(1/2):582-586. |
| [13] | Qiang Yuan;Caijun Shi;Geert De Schutter;Katrien Audenaert;Dehua Deng.Chloride Binding Of Cement-based Materials Subjected To External Chloride Environment - A Review[J].Construction and Building Materials,20091(1):1-13. |
| [14] | Obada Kayali;M.S.H. Khan;M. Sharfuddin Ahmed.The role of hydrotalcite in chloride binding and corrosion protection in concretes with ground granulated blast furnace slag[J].Cement & concrete composites,20128(8):936-945. |
| [15] | Morimoto, K.;Anraku, S.;Hoshino, J.;Yoneda, T.;Sato, T..Surface complexation reactions of inorganic anions on hydrotalcite-like compounds[J].Journal of Colloid and Interface Science,2012:99-104. |
| [16] | Chen W;Brouwers HJH.The hydration of slag, part 1: reaction models for alkali-activated slag[J].Journal of Materials Science,20072(2):428-443. |
| [17] | C. A. JOHNSON;F. P. GLASSER.HYDROTALCITE-LIKE MINERALS (M_2Al(OH)_6(CO_3)_(0.5) .XH_2O, WHERE M = Mg, Zn, Co, Ni) IN THE ENVIRONMENT: SYNTHESIS, CHARACTERIZATION AND THERMODYNAMIC STABILITY[J].Clays and clay minerals,20031(1):1-8. |
| [18] | F.P.Glasser;A.Kindness.Stability and solubility relationships in Afm phases Part I. Chloride, sulfate and hydroxide[J].Cement and Concrete Research,19996(6):861-866. |
| [19] | M. Ben Haha;B. Lothenbach;G. Le Saout.Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag - Part I: Effect of MgO[J].Cement and Concrete Research,20119(9):955-963. |
| [20] | 钱觉时;别安涛;李昕成.水泥混凝土中MgO来源与作用的研究进展[J].材料导报,2010(11):128-131. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%