采用Ti3SiC2与Ti3AlC2粉体和cBN粉体为原料,通过微波烧结制备Ti3SiC2与Ti3AlC2结合剂cBN复合材料,同时研究cBN的含量对该复合材料的物相组成与显微形貌的影响.结果表明,Ti3SiC2-cBN试样烧结后得到了SiC、TiSi2、TiC、TiO、TiO2、SiO2.cBN添加量为10%的复合材料中Ti3SiC2分解较为严重.试样烧结后基体组织比较细小,只有几微米.当原料中cBN含量为20%时,cBN表面会形成凹凸不平的组织.Ti3AlC2-cBN试样烧结后得到了Ti2 AlC、TiC、Ti、Al、Al2 O3,Ti3 AlC2材料分解完全.cBN含量较高时,它可以与Ti3AlC2或其分解产物充分反应,形成相应的氮化物或碳氮化物.

Ti3SiC2 and Ti3AlC2 ceramic boned cBN composites were fabricated by microwave sintering from Ti3 SiC2 ,Ti3AlC2 and cBN raw powders.The effect of cBN′s content on phase and micro-structure of composites were also studied.The result shows that SiC,TiSi2 ,TiC,TiO,TiO2 ,SiO2 could be synthesized after microwave sintering of Ti3 SiC2-cBN samples.When cBN content was 10%,Ti3 SiC2 was decomposed seriously.The phase organization was finer with a size of about several micrometer.When cBN content was 20%,irregularity organization were formed on the surface of Ti2 AlC,TiC,Ti,Al,Al2 O3 could be synthesized after microwave sintering of Ti3 AlC2-cBN samples. Ti3AlC2 was decomposed totally.When cBN content was higher,it can react with Ti3AlC2 or its decomposed products fully to form nitride or carbonitride.

参考文献

[1] Michel W.Barsoum.The M_(N+1)AX_N Phases: A new Class of solids; Thermodynamically Stable Nanolaminates[J].Progress in Solid State Chemistry,20001/4(1/4):201-281.
[2] Barsoum MW.;Elraghy T..SYNTHESIS AND CHARACTERIZATION OF A REMARKABLE CERAMIC - TI3SIC2[J].Journal of the American Ceramic Society,19967(7):1953-1956.
[3] Gao N.F. -;Zhang D;Miyamoto Y.Dense Ti sub 3 SiC sub 2 prepared by reactive HIP[J].Journal of Materials Science,199918(18):4385-4392.
[4] W.B. Zhou;B.C. Mei;J.Q. Zhu.Fabrication of high-purity ternary carbide Ti_3SiC_2 by spark plasma sintering technique[J].Materials Letters,200512(12):1547-1551.
[5] Yan Ming;Mei Bingchu;Zhu Jiaoqun.Synthesis of high-purity bulk Ti_2AlN by spark plasma sintering (SPS)[J].CERAMICS INTERNATIONAL,20086(6):1439-1442.
[6] 李正阳;周爱国;李良;王李波.无压烧结制备Ti3SiC2-金刚石复合材料的反应机理与微观结构[J].兵器材料科学与工程,2013(6):29-31.
[7] Tokoloho Rampai;C.I. Lang;Iakovos Sigalas.Investigation of MAX phase/c-BN composites[J].CERAMICS INTERNATIONAL,20135(5):4739-4748.
[8] Fangzhi Li;Haibin Zhang;Qian Wang.Microwave Sintering of Ti_3Si(AI)C_2 Ceramic[J].Journal of the American Ceramic Society,20149(9):2731-2735.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%