在不同浇注温度和电磁搅拌制度下制备了A356铝合金半固态浆料,研究了微量稀土下浇注温度、电磁搅拌频率和时间对半固态A356铝合金初生相形貌及力学性能的影响.结果表明,通过优化半固态制浆工艺条件减少稀土的加入量是可行的,实验表明稀土微量化的合适工艺方案是:浇注温度为630℃,电磁搅拌频率为30 Hz,搅拌时间为8 s.此时,加入量为0.3%的稀土La细化效果和常规加入量为0.4%La的低过热度浇注的相当,其力学性能也基本相同.
The semisolid slurry of A356 alloys were prepared at different pouring temperatures and electromag-netic stirring processes.The morphologies of primary phase and mechanical properties of the semisolid A356 alloy were investigated under the pouring temperature,electromagnetic stirring frequency and treated time with the trace RE.The results showed that,it was feasible to reduce the addition amount of RE by optimizing the semisolid slurry process conditions.The suitable preparing parameters were obtained by the experiment,in which the pouring tempe-rature was 630 ℃,the frequency of electromagnetic stirring was 30 Hz,and the stirring treated time was 8 s.At this point,when the content of La addition was 0.3%,the modification effects of the semisolid A356 alloy was indistin-guishable with the conventional addition amount of 0.4% La in low superheat pouring,and their mechanical properties were close to each other.
参考文献
| [1] | 王丽萍;曹国剑;张建交;王国军;吕新宇;郭二军.RE-Ba-Sb复合变质对4004铝合金组织与性能的影响[J].中国有色金属学报（英文版）,2013(8):2236-2242. |
| [2] | 付莹;接金川;张宇博;钟德水;李继展;李廷举.物理场对3003/4004复合铸锭凝固组织的影响[J].中国有色金属学报（英文版）,2013(9):2496-2501. |
| [3] | S. Nourouzi;H. Baseri;A. Kolahdooz;S. M. Ghavamodini.Optimization of semi-solid metal processing of A356 aluminum alloy[J].Journal of Mechanical Science and Technology,201312(12):3869-3874. |
| [4] | LIU Zheng;MAO Wei-min;ZHAO Zheng-duo.Effect of pouring temperature on semi-solid slurry of A356 Al alloy prepared by weak electromagnetic stirring[J].中国有色金属学会会刊（英文版）,2006(01):71-76. |
| [5] | Mousavi, G.S.;Emamy, M.;Rassizadehghani, J..The effect of mischmetal and heat treatment on the microstructure and tensile properties of A357 Al-Si casting alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:573-581. |
| [6] | LIU Zheng;HU Yongmei.Effect of yttrium on the microstructure of a semi-solid A356 Al alloy[J].稀有金属（英文版）,2008(05):536-540. |
| [7] | Liu Zheng;Mao Weimin.Effect of pouring temperature on semi-solid slurry of ZL101 alloy prepared by slightly electromagnetic stirring[J].中国铸造,2009(01):9-14. |
| [8] | Zhong-wei Chen;Cui-ying Ma;Pei Chen.Modifying agent selection for Al-7Si alloy by Miedema model[J].矿物冶金与材料学报,2012(02):131-135. |
| [9] | 刘政;许鹤君.电磁搅拌时间对半固态A356合金凝固组织的影响[J].特种铸造及有色合金,2012(9):828-832. |
| [10] | 张帆;康永林;杨柳青;丁瑞华.浇注温度对合金熔体冷却规律和半固态组织的影响[J].北京科技大学学报,2010(11):1453-1458. |
| [11] | YANG Xiao-rong;MAO Wei-min;PEI Sheng.Influence of process parameters on microstructure of semisolid A356 alloy slug cast through vertical pipe[J].中国有色金属学会会刊（英文版）,2008(01):99-103. |
| [12] | Xiaowu HU;Fanrong AI;Hong YAN.Influences of pouring temperature and cooling rate on microstructure and mechanical properties of casting Al-Si-Cu aluminum alloy[J].金属学报（英文版）,2012(4):272-278. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%