增稠是纤维素醚对水泥基材料的重要改性效果.研究了纤维素醚掺量、粘度仪旋转速度和温度对纤维素醚改性水泥浆粘度变化的影响.结果表明:纤维素醚掺量增加,水泥浆的粘度不断增加,纤维素醚溶液和水泥浆的粘度具有“复合叠加效应”;纤维素醚改性水泥浆的假塑性低于纯水泥浆,粘度仪的旋转速度越低,或纤维素醚改性水泥浆的粘度越低,或纤维素醚掺量越低,纤维素醚改性水泥浆的假塑性越明显;温度升高,由于温度和水泥水化的共同作用,纤维素醚改性水泥浆的粘度会增加或降低.纤维素醚的种类不同,其改性水泥浆的粘度变化规律存在差异.
参考文献
[1] | 蹇守卫;马保国;苏雷;李相国;穆松;袁龙.纤维素醚改性砂浆的研究进展[J].硅酸盐通报,2011(3):560-566. |
[2] | M. Saric-Coric;K.H. Khayat;A. Tagnit-Hamou.Performance characteristics of cement grouts made with various combinations of high-range water reducer and cellulose-based viscosity modifier[J].Cement and Concrete Research,200312(12):1999-2008. |
[3] | H. Paiva;L.M. Silva;J.A. Labrincha.Effects of a water-retaining agent on the rheological behaviour of a single-coat render mortar[J].Cement and Concrete Research,20067(7):1257-1262. |
[4] | H. Paiva;L.P. Esteves;P.B. Cachim;V.M. Ferreira.Rheology And Hardened Properties Of Single-coat Render Mortars With Different Types Of Water Retaining Agents[J].Construction and Building Materials,20092(2):1141-1146. |
[5] | Laetitia Patural;Philippe Marchal;Alexandre Covin.Cellulose ethers influence on water retention and consistency in cement-based mortars[J].Cement and Concrete Research,20111(1):46-55. |
[6] | 郑文杰;叶君;何婉芬;刘道恒.羟乙基纤维素水溶液的流变性能的研究[J].造纸科学与技术,2007(1):40-42. |
[7] | 叶君;熊犍;伍红;何婉芬;禤智勇.羟乙基纤维素水溶液粘度特性的研究[J].造纸科学与技术,2004(6):50-52. |
[8] | 欧志华;毛泰威;刘锡军;王彦.干混砂浆用纤维素醚溶液的黏度测试方法探讨[J].湖南工业大学学报,2015(3):15-19. |
[9] | Ou Zhi Hua;Ma Bao Guo;Jian Shou Wei.Influence of cellulose ethers molecular parameters on hydration kinetics of Portland cement at early ages[J].Construction and Building Materials,2012:78-83. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%