对异种钢不同板厚涂胶与未涂胶DP600双相钢和超低碳DC54D电阻点焊进行了研究。深入分析了不同焊接时间下焊接接头显微组织、显微硬度、拉剪性能及扫描断口。研究结果表明,随着焊接时间的延长,焊点直径增大。当焊接时间为2周波时,热影响区为“半月形”,延长焊接时间,熔核形状由“蝶形”转变为“椭型”。由于DC54D对熔核区碳含量的稀释作用,熔核区显微硬度低于热影响区硬度。拉伸-剪切试验中,当焊接时间为13-19周波时,涂胶与未涂胶接头拉剪强度趋于稳定。未涂胶接头的最大拉剪强度为5.45 kN,涂胶接头的最大拉剪强度为5.15 kN。当焊接电流为9 kA、电极压力为2.6 kN、焊接时间为13-19周波时,涂胶的焊接接头能得到优异的力学性能,但是比未涂胶接头略差。未涂胶与涂胶接头断裂均发生在DC54D侧。
Joining of a dual-phase steel DP600 and an ultra-low carbon steel DC54D dissimilar couple was inves-tigated by RSW in current study.The microstructure,micro-hardness and tensile-shear properties were analyzed in-depth.The results show that the weld diameter increased as the welding time prolonged.The heat-affected zone ex-hibited lune shape when the welding time was 2 cycles.With the increase of welding time,the weld was changed from butterfly shape to elliptic shape.The micro-hardness of the fusion zone was lower than that of the heat-affected zone due to the dilution of DC54D.In tensile-shear testing,the tensile-shear strength tended to be stable when the welding time was 13-19 cycles.The largest tensile-shear strength was 5.15 kN and 5.45 kN of glued and un-glued welded spot,respectively.When the welding current,electrode force was 9 kA and 2.6 kN,and the welding time was 13-19 cycles,the glued resistance spot welded joint could gain a well mechanical properties but worse than the un-glued. Both of the glued and un-glued welds fractured on DC54D side.
参考文献
| [1] | 徐士航;王敏;施天寅;潘华;雷鸣.DP590GA热镀锌双相钢电阻点焊接头性能[J].电焊机,2009(10):70-73. |
| [2] | 李鑫;张勇;叶成涛.基于PLC的车身气动焊装夹具设计[J].重庆理工大学学报：自然科学,2011(12):12-18. |
| [3] | 刘文华;何天明.高强度钢在汽车轻量化中的应用[J].汽车工艺与材料,2008(11):49-51. |
| [4] | 杨思源;涂雄;李军.尺寸工程在白车身制造过程中的应用[J].重庆理工大学学报：自然科学,2012(6):18-23. |
| [5] | Rocha RO;Melo TMF;Pereloma E;Santos DB.Microstructural evolution at the initial stages of continuous annealing of cold rolled dual-phase steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20051/2(1/2):296-304. |
| [6] | 张梅;符仁钰;许洛萍.汽车用双相钢钢板的发展[J].热处理,2001(1):5-8. |
| [7] | 李守华;李俊.汽车用高强度IF钢的研究进展[J].上海金属,2007(5):66-70. |
| [8] | 胡远志;雷雨;郑光泽;刘卫国;冯擎峰;刘西.车身密封性对车内噪声的影响[J].重庆理工大学学报（自然科学版）,2014(9):1-6. |
| [9] | 帅歌旺;周平建;刘建彬.电阻点焊电极的研究进展与发展趋势[J].材料导报,2015(7):59-62,70. |
| [10] | 王晓宁.浅谈点焊密封胶在白车身制造中的应用[J].粘接,2013(12):89-91,88. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%