通过SEM、电化学方法以及XRD半定量分析方法,对在城市大气(武汉站)和工业大气(石化站)中曝晒早期的Q235碳钢和耐候钢锈层初期演化机制进行研究.与Q235碳钢相比,耐候钢在条件恶劣石化环境中更快体现耐候性,而在武汉站暴晒初期耐候钢腐蚀速率较Q235碳钢快.在含S高的石化环境,对于α-FeOOH形成有一定催化作用.另外发现锈层初期的氧化还原反应分为两个阶段.第一个阶段锈层还原产物的氧化较快,而第二个阶段,还原产物Fe3O4积累,氧化过程受阻,并且锈层整体电化学活性有所升高.
参考文献
[1] | Yuantai Ma;Ying Li;Fuhui Wang .Corrosion of low carbon steel in atmospheric environments of different chloride content[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(5):997-1006. |
[2] | Long Hao;Sixun Zhang;Junhua Dong;Wei Ke .Evolution of atmospheric corrosion of MnCuP weathering steel in a simulated coastal-industrial atmosphere[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(Jun.):270-276. |
[3] | Long Hao;Sixun Zhang;Junhua Dong;Wei Ke .Evolution of corrosion of MnCuP weathering steel submitted to wet/dry cyclic tests in a simulated coastal atmosphere[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(may):175-180. |
[4] | K.E. Garcia;C.A. Barrero;A.L. Morales;J.M. Greneche .Lost iron and iron converted into rust in steels submitted to dry-wet corrosion process[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(3):763-772. |
[5] | T. Kamimura;S. Hara;H. Miyuki;M. Yamashita;H. Uchida .Composition and protective ability of rust layer formed on weathering steel exposed to various environments[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(9):2799-2812. |
[6] | Q.X. Li;Z.Y. Wang;W. Han;E.H. Han .Characterization of the rust formed on weathering steel exposed to Qinghai salt lake atmosphere[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(2):365-371. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%