为开发先进的铝基固体自润滑材料与技术,采用亚音速火焰喷涂技术制备了铝硅/聚苯酯涂层,利用扫描电子显微镜(SEM)、电子能谱仪(EDS)、洛氏硬度计、拉伸试验机、摩擦磨损试验机分析测试了涂层的组织、硬度与结合强度,探讨了载荷对涂层摩擦学性能的影响.结果表明,涂层由铝硅和聚苯酯相构成,聚苯酯相所占面积比约20%.涂层组织致密,与基体结合强度达67 MPa,表面宏观硬度约为75.3 HR15Y.试验载荷对铝硅/聚苯酯涂层的摩擦学性能有显著影响,涂层摩擦因数随载荷的上升呈先下降后上升趋势,不同载荷致使涂层在组织、成分、形态等方面的差异是其主要影响因素.
参考文献
[1] | Shengyu Zhu;Qinling Bi;Jun Yang;Weimin Liu.Influence of Cr content on tribological properties of Ni_3Al matrix high temperature self-lubricating composites[J].Tribology International,201110(10):1182-1187. |
[2] | Jian Liang Li;Dang Sheng Xiong.Tribological properties of nickel-based self-lubricating composite at elevated temperature and counterface material selection[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20083/4(3/4):533-539. |
[3] | 顾明亮 .镍包石墨自润滑涂层摩擦磨损性能研究[D].江南大学,2008. |
[4] | 尹延国 .铜基石墨自润滑材料及其摩擦学研究[D].合肥工业大学,2006. |
[5] | 王月 .铝硅封严涂层热稳失效机理分析[D].天津大学,2009. |
[6] | M. Bounazef;S. Guessasma;B. Ait Saadi.The wear, deterioration and transformation phenomena of abradable coating BN-SiAI-bounding organic element, caused by the friction between the blades and the turbine casing[J].Materials Letters,200427/28(27/28):3375-3380. |
[7] | Johnston, R.E..Mechanical characterisation of AlSi-hBN, NiCrAl-Bentonite, and NiCrAl-Bentonite-hBN freestanding abradable coatings[J].Surface & Coatings Technology,201110(10):3268-3273. |
[8] | 朱立群;刘孟兰;王建华;李雪源;沈德逵;宋定宇.飞机发动机封严涂层的研究[J].航空学报,2000(Z1):85-89. |
[9] | J.J. Tang;K. Liu;Q.Z. Yang;Y.H.Wang;P. Zhang;Y.Wang;L. Zhao;Q.Q. Fu;Z.H. Han;Y. Bai.The influence of size and distribution of graphite on the friction andwear behavior of Ni-graphite coatings[J].Surface & Coatings Technology,2014:48-55. |
[10] | Yang, Jie;Zhang, Yunjing;Zhao, Xiaoqin;An, Yulong;Zhou, Huidi;Chen, Jianmin;Hou, Guoliang.Tribological behaviors of plasma sprayed CuAl/Ni-graphite composite coating[J].Tribology International,2015:96-103. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%