以SiO2为载体,铜氨溶液为前驱体,采用蒸氨法在不同蒸氨压力下制备了系列铜负载量质量分数为20.0%的Cu/SiO2催化剂.采用X射线衍射(XRD)、H2-程序升温还(H2-TPR)、高分辨透射电子显微镜(HRTEM)、X射线诱导俄歇电子能谱(XAES)等技术手段对催化剂的物理化学性能进行了表征.考察了蒸氨速率对催化剂物化结构及其草酸二甲酯催化加氢制乙二醇的催化性能影响.在反应温度200℃、压力3.0 MPa、液时空速LHSV=0.4 h-、氢气草酸二甲酯摩尔比80:1的反应条件下测定了催化剂的活性.结果表明,在蒸氨压力为31.3 kPa条件下制备的催化剂表现出了最佳活性和选择性,草酸二甲酯转化率达到了99.9%,乙二醇选择性达94.4%.H2-TPR、XRD、TEM、FTIR及XAES表征结果表明,较低蒸氨压力有利于铜氨离子快速分解负载在载体上,避免铜粒子聚集长大,还原后形成Cu2O和Cu0物种颗粒尺寸较小,分散比较均匀,催化活性,尤其是乙二醇的选择性更佳.
参考文献
[1] | 黄格省;李振宇;李顶杰;梁川.石油和煤生产乙二醇技术现状及产业前景分析[J].化工进展,2011(7):1461-1465. |
[2] | 宋河远;靳荣华;康美荣;陈静.碳一化工路线制备乙二醇研究进展[J].催化学报,2013(6):1035-1050. |
[3] | 林凌;潘鹏斌;周张锋;李兆基;杨锦霞;孙明玲;姚元根.溶胶凝胶法制备的Cu/SiO2催化剂及其催化草酸二甲酯加氢反应[J].催化学报,2011(6):957-969. |
[4] | 王保伟;张旭;许茜;许根慧.Cu/SiO2催化剂的制备、表征及其对草酸二乙酯加氢制乙二醇的催化性能[J].催化学报,2008(3):275-280. |
[5] | Chen LF;Guo PJ;Qiao MH;Yan SR;Li HX;Shen W;Xu HL;Fan KN.CU/SiO2 catalysts prepared by the ammonia-evaporation method: Texture, structure, and catalytic performance in hydrogenation of dimethyl oxalate to ethylene glycol[J].Journal of Catalysis,20081(1):172-180. |
[6] | Xinbin Ma;Hanwen Chi;Hairong Yue.Hydrogenation of Dimethyl Oxalate to Ethylene Glycol over Mesoporous Cu-MCM-41 Catalysts[J].AIChE Journal,20137(7):2530-2539. |
[7] | Li Zhao;Yujun Zhao;Shengping Wang.Hydrogenation of Dimethyl Oxalate Using Extruded Cu/SiO2 Catalysts: Mechanical Strength and Catalytic Performance[J].Industrial & Engineering Chemistry Research,201243(43):13935-13943. |
[8] | Feng Li;Chun-Shan Lu;Xiao-Nian Li.The effect of the amount of ammonia on the Cu0/Cu+ ratio of Cu/SiO2 catalyst for the hydrogenation of dimethyl oxalate to ethylene glycol[J].中国化学快报(英文版),2014(11):1461-1465. |
[9] | Zhao, S.;Yue, H.;Zhao, Y.;Wang, B.;Geng, Y.;Lv, J.;Wang, S.;Gong, J.;Ma, X..Chemoselective synthesis of ethanol via hydrogenation of dimethyl oxalate on Cu/SiO_2: Enhanced stability with boron dopant[J].Journal of Catalysis,2013:142-150. |
[10] | 李竹霞;钱志刚;赵秀阁;肖文德.载体对草酸二甲酯加氢铜基催化剂的影响[J].华东理工大学学报(自然科学版),2005(1):27-30,51. |
[11] | Anyuan Yin;Xiaoyang Guo;Wei-Lin Dai.Effect of initial precipitation temperature on the structural evolution and catalytic behavior of Cu/SiO2 catalyst in the hydrogenation of dimethyloxalate[J].Catalysis Communications,20116(6):412-416. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%