为探索提高SiCp／Fe力学性能的途径，采用包覆混料工艺，研究了该工艺对镀铜SiCp／Fe力学性能的影响，以及该工艺下增强粒子混合尺寸的影响．结果表明：包覆混料相比于普通混料，可显著改善SiC粒子在基体中分散的均匀性，而镀铜的作用是显著消除界面缺陷；性能的改善是包覆混料改善粒子分散性和镀铜改善界面结合的综合结果．对于体积分数30％SiCp／Fe的抗拉强度，通过包覆改善均匀性的贡献可提高7．2％，通过镀铜消除界面缺陷的贡献可提高12．5％，因此减少界面缺陷对颗粒增强复合材料力学性能的提高更重要．混合尺寸粒子对力学性能的增强效果明显高于其对应单一尺寸，这是由于小尺寸粒子能有效地提高基体的强度，而大尺寸颗粒更有效地承担载荷传递的作用．
To improve the mechanical properties of the SiCp/Fe composites, the effect of high?energy ball milling processing on the mechanical properties of copper?coated SiC particles reinforced iron matrix composites were investigated, and the effect of size mixture of copper?coated SiC particles on the properties of the composites was discussed as well. The results shows that the properties of composites have been improved by the high?energy ball milling that can also improve the uniformity of SiC particles distribution in the composites. The copper coating on the SiC particle surface can reduce the interfacial defects of the composites which is helpful for the improvement of mechanical properties of the composites. The tensile strength of the composites is increased by 7. 2% because of the uniformity of SiC particles distribution and by 12. 5% because of the reducing of interfacial defects which is more evident. The mechanical property of the composites reinforced by the mixture?sized SiC particles was higher than that of the composites reinforced by the related single?sized particles because the smaller?sized SiC particles tend to improve the strength of the matrix and the larger?sized SiC particles carry and transfer more load.
参考文献
| [1] | NIU L B, HOJAMBERDIEV M, XU Y H. Preparation of in situ-formed WC/Fe composite on gray cast iron substrate by a centrifugal casting process [J]. Journal of Materials Processing Technology, 2010, 210 (14):1986-1990.,2010. |
| [2] | LIU J, LI J, XU C Y. Interaction of the cutting tools and the ceramic-reinforced metal matrix composites during micro-machining:A review [J]. Journal of Manufacturing Science and Technology, 2014, 7 (2):55-70.,2014. |
| [3] | ZHONG L S, YE F X, XU Y H, et al. Microstructure and abrasive wear characteristics of in situ vanadium carbide particulate-reinforced iron matrix composites [J]. Materials and Design, 2014, 54:564-569.,2014. |
| [4] | GUL H, KIHC F, UYSAL M, et al. Effect of particle concentration on the structure and tribological properties of submicron particle SiC reinforced Ni metal matrix composite (MMC) coatings produced by electrodeposition[J]. Applied Surface Science, 2012, 258(10):4260-4267.,2012. |
| [5] | PELLEG J. Reactions in the matrix and interface of the Fe-SiC metal matrix composite system [J]. Materials Science and Engineering A, 1999, 269(1/2):225-241.,1999. |
| [6] | WANG Y Q, WANG X J, GONG W X, et al. Effect of SiC particles on microarc oxidation process of magnesium matrix composites [J]. Applied Surface Science, 2013, 283:906-913.,2013. |
| [7] | AKRAMIFARD H R, SHAMANIAN M, SABBAGHIAN M, et al. Microstructure and mechanical properties of Cu/SiC metal matrix composite fabricated via friction stir processing [J]. Materials and Design, 2014, 54:838-844.,2014. |
| [8] | SONG B, DONG S J, CODDET P, et al. Microstruc-ture and tensile behavior of hybrid nano-micro SiC re-inforced iron matrix composites produced by selective laser melting[J]. Journal of Alloys and Compounds, 2013, 579:415-421.,2013. |
| [9] | CHANDRASEKARAN M, SINGH P. Sintered iron-based antifriction materials with added β-SiC [J]. Wear, 1997, 206 (1/2):1-7.,1997. |
| [10] | MIYAUCHI T, TSUJIMURA T, HANDA K, et al. Influence of silicon carbide filters in cast iron composite brake blocks on brake performance and development of a production process[J]. Wear, 2009, 267(5/6/7/8):833-838.,2009. |
| [11] | ZHUANG W B, ZONG B Y, WANG Y M, et al. Processing and properties of SiCp/Fe composites by resistance sintering with a novel dynamic temperature control[J]. Journal of Composite Materials, 2012, 47 (8):1001-1010.,2012. |
| [12] | LI J, ZONG B Y, WANG Y M, et al. Experiment and modeling of mechanical properties on iron matrix composites reinforced by different types of ceramic particles [J]. Materials Science and Engineering A, 2010, 527(29/30):7545-7551.,2010. |
| [13] | 庄伟彬,宗亚平,张跃波,曹新建.铁基复合材料碳化硅粒子混合尺寸增强作用机理[J].材料科学与工程学报,2013(01):1-5,141. |
| [14] | 李杰,宗亚平,王耀勉,庄伟彬.不同颗粒增强铁基复合材料磨损性能的对比[J].东北大学学报（自然科学版）,2010(05):660-664. |
| [15] | 庄伟彬,宗亚平,张跃波,曹新建.机械冲击包覆工艺对SiCp/Fe复合材料组织性能的影响[J].东北大学学报（自然科学版）,2013(05):663-668. |
| [16] | 张跃波,宗亚平,曹新建,张龙.碳化硅颗粒化学镀镍对铁基复合材料性能的影响[J].材料研究学报,2012(05):483-488. |
| [17] | GU Jinhai, ZHANG Xiaonong, GU Mingyuan, et al. Internal friction peak and damping mechanism in high damping 6061Al/SiCp/Gr hybrid metal matrix composite [J]. Journal of Alloys and Compounds, 2004, 372 (1/2):304-308.,2004. |
| [18] | SCHALLER R. Metal matrix composites, a smart choice for high damping materials [J]. Journal of Alloys and Compounds, 2003, 355(1/2):131-135.,2003. |
| [19] | ZHANG Y B, ZONG B Y, JIN J F, et al. Effect of particulate reinforcement electroless plating on properties of SiC/Fe composite[J]. Applied Mechanics and Materials, 2014, 556-562:302-305.,2014. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%