在国产 EA4T 车轴钢上截取光滑和缺口疲劳试样,按照 EN13261-2009标准测试了其旋转弯曲疲劳性能,并观察了断口形貌。结果表明:国产 EA4T 车轴钢的光滑和缺口疲劳强度均满足 EN13261-2009的要求,缺口试样的疲劳强度比光滑试样的低30%左右;光滑试样的裂纹萌生于试样表面,呈单源开裂,缺口试样的裂纹萌生于缺口根部,呈多源开裂;未断缺口试样的缺口根部存在非扩展性裂纹。

The rotating bending fatigue property of smooth and notched specimens cut from domestic EA4T axle steel was tested according to the standard of EN13261 -2009 and the fracture morphology was observed.The results show that the fatigue strength of the domestic EA4T axle steel met the requirements of EN13261 -2009, and the fatigue strength of the notched specimen was 30% less than that of the smooth specimen;the rotating bending fatigue cracks initiated from a single source on the surface of the smooth specimen,while the cracks in notched specimen were originated from several points around the notch root;non propagating cracks were also observed at the notch root of the non fractured notched specimen.

参考文献

[1] 魏安安,纪熙,李艳斌,汪磊.带缺口构件疲劳寿命的研究进展[J].机械工程材料,2011(03):1-3,31.
[2] NOVOSAD M;FAJKOS R;REHA B et al.Fatigue tests of railway axles[J].Procedia Engineering,2010,2(1):2259-2268.
[3] MADIA M;BERETTA S;SCH?DEL M .Stress intensity factor solutions for cracks in railway axles[J].Engineering Fracture Mechanics,2011,78(5):764-792.
[4] 张俊清,周素霞,谢基龙.缺口对车轴钢疲劳性能的影响[J].北京交通大学学报,2010(04):132-135.
[5] 黄国,黄海明,王超,李玮洁.45#车轴钢疲劳性能试验研究[J].中国铁道科学,2013(04):71-76.
[6] 何忠,姚伟伟.LZ50钢车轴的旋转弯曲疲劳性能[J].机械工程材料,2012(01):94-96,100.
[7] PILKEY W D.Peterson′s Stress Concentration Factors[M].New York:John Wiley & Sons Inc,1997:123-123.
[8] SURESH S;RITCHIE R O .Propagation of short fatigue cracks[J].International Metals Reviews,1984,29(1):445-475.
[9] HADDAD M H E;TOPPER T H;SMITH K N .Prediction of non propagation cracks[J].Engineering Fracture Mechanics,1979,11(3):573-584.
[10] 李锋,何宇廷,范超华,李鸿鹏,崔荣洪.疲劳小裂纹理论及其应用[J].机械工程材料,2007(11):6-9.
[11] ELBER W .The significance of fatigue crack closure[J].ASTM STP,1971,486:230-242.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%