首先通过化学氧化法制备本征态聚苯胺(EB),然后利用4种质子酸(DBSA、SSA、HCl、H 3 PO 4)对 EB 进行二次掺杂制备了二次掺杂聚苯胺(PANI),通过研究质子酸浓度、掺杂时间和掺杂温度对二次掺杂 PANI 电导率的影响,得到了最适宜的二次掺杂条件,并考察了最适宜掺杂条件下制备的二次掺杂 PANI 的结构和形貌.结果表明：最适宜的二次掺杂条件为掺杂剂浓度1．0 mol?L－1,掺杂时间6 h,掺杂温度为25℃,此时二次掺杂 PANI 的电导率最高,其中 DBSA 二次掺杂 PANI 的电导率最高,为3．301 S?cm－1；与 EB 相比,二次掺杂 PANI 的红外特征峰变宽且向低频移动；DBSA 二次掺杂 PANI 的结晶度最高,其微观结构由较为分散的圆形颗粒组成.
Eigenstate polyaniline was prepared by chemical oxidation method,and then was doped by four kinds of protonic acids (hydrochloric acid,phosphate acid,dodecylbenzene sulfonate acid and sulfosalicylic acid)to prepare dual-doped polyaniline (PANI).The most suitable doping conditions were obtained by studying the effects of protonic acids concentration,adopping time and temperature on conductivity of dual-doped PANI.Moreover,the structure and morphology of dual-doped PANI obtained under the most suitable conditions were investigated.The results indicate that the most suitable doping conditions were adoping condition of 1.0 mol?L-1 ,doping temperature of 25 ℃,doping time of 6 h.Dual-doped PANI obtained under the most suitable conditions had the highest conductivity,was 3.301 S?cm-1 .Compared with eigenstate polyaniline,the infrared characteristic peaks of dual doped PANI was wider and moved to low frequency.DBSA doped PANI had the highest crystallinity,and its microstructure was composed of scattered round particles.
参考文献
| [1] | Maocheng Yan;Christopher A. Vetter;Victoria J. Gelling.Corrosion inhibition performance of polypyrrole Al flake composite coatings for Al alloys[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2013May(May):37-45. |
| [2] | 史洪微;刘福春;王震宇;郝永胜;张帆;韩恩厚;柯伟.海洋防腐涂料的研究进展[J].腐蚀科学与防护技术,2010(1):43-46. |
| [3] | 杨显;杨小刚;马新起.功能酸二次掺杂聚苯胺的防腐蚀性能[J].化工学报,2014(9):3738-3743. |
| [4] | 李靖;方鲲;邱宏;毛卫民;吴其晔.掺杂态聚苯胺（Doped-PANI）的电导率-温度特性和形态结构研究[J].材料工程,2006(z1):117-119,123. |
| [5] | 唐晓萍.磷酸掺杂对聚苯胺电导率及微观结构的影响[J].西南民族学院学报(自然科学版),2003(02):164-166. |
| [6] | 孙建平;李宝铭;吴洪才.十二烷基苯磺酸掺杂聚苯胺的性能研究[J].精细化工,2002(10):578-580. |
| [7] | 黄惠;许金泉;刘小丽;郭忠诚.复合酸掺杂导电聚苯胺的性能研究[J].化学通报（印刷版）,2009(8):744-748. |
| [8] | 陈德贤;郑玉婴;张通;李宝铭.磺基水杨酸掺杂导电聚苯胺纳米材料的制备与性能研究[J].功能材料,2012(11):1373-1377. |
| [9] | Y.F. Huang;C.W. Lin.Exploration of the formation mechanisms of polyaniline nanotubes and nanofibers through a template-free method[J].Synthetic Metals,200917/18(17/18):1824-1830. |
| [10] | 杨军;何志伟;吕秋丰.聚苯胺-木质素磺酸纳米复合物的制备及吸附性能[J].化工学报,2013(6):2264-2269. |
| [11] | 罗丞 .掺杂聚苯胺/环氧树脂防腐涂料制备与防腐性能研究[D].哈尔滨工程大学,2011. |
| [12] | Lee YM.;Kang JS.;Ha SY.;Kim JH..Annealing effects of dilute polyaniline/NMP solution[J].Macromolecules,200020(20):7431-7439. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%