某 Q235钢天然气管道运行10 a 后发生了泄漏，采用表面宏观形貌观察、力学性能测试、金相检验、硬度及残余应力检验等方法分析了管道开裂的原因。结果表明：管道的开裂为焊接质量存在严重问题而导致的脆性开裂；焊接残余应力和工作应力、组装应力叠加形成的局部高应力是管道失效的根本原因；采用适当的焊接工艺、焊后消除应力处理等措施，可降低管道开裂的几率。
After using for 10 years,a Q235 steel natural gas pipeline leakage occured,the cracking cause was analyzed by macrograph examination,mechanical property testing,microscopic examination and residual stress testing.The results show that the cracking mode was brittle cracking caused by serious welding quality.Localized high stress formed by welding residual stress,work stress and assemble stress was the basic failure cause.Adopting appropriate welding process and eliminating stress after welding could reduce the risk of pipeline cracking.
参考文献
| [1] | 王旭东;徐杰;孙冬柏;孟惠民;俞宏英;樊自拴.国外油气管道缺陷评估方法评介[J].机械工程材料,2009(4):6-9,13. |
| [2] | James F. Wilson.Failure Analysis of a Buried Pipeline Transporting Gas[J].Journal of pipeline systems engineering and practice,20121(1):17-21. |
| [3] | E. Sadeghi Meresht;T. Shahrabi Farahani;J. Neshati.Failure analysis of stress corrosion cracking occurred in a gas transmission steel pipeline[J].Engineering failure analysis,20113(3):963-970. |
| [4] | Z.A. Majid;R. Mohsin;Z. Yaacob.Failure analysis of natural gas pipes[J].Engineering failure analysis,20104(4):818-837. |
| [5] | 姚宏;刘荣.埋地燃气管道失效分析的研究[J].贵州工业大学学报（自然科学版）,2005(3):121-124. |
| [6] | 李月娥;袁鹏斌;颜达峰;舒江;刘乃勇.埋地钢质天然气管道失效分析[J].全面腐蚀控制,2013(1):49-53. |
| [7] | 汪建华;陆皓.焊接残余应力形成机制与消除原理若干问题的讨论[J].焊接学报,2002(3):75-79. |
| [8] | 高怡斐.仪器化压痕试验法测定金属材料的硬度与材料参数[J].物理测试,2003(05):1-3,10. |
| [9] | 李和平;杨晓晨;李颖;李建龙.仪器化压痕技术的发展和面临的问题[J].工程与试验,2011(z1):3-6,62. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%