在Mg-1.3Mn-1.0Ce-4.0Zn合金熔体中加入质量分数为0~1.5%的碳纳米管(CNTs),采用搅拌铸造法制备了碳纳米管增强镁基复合材料,研究了复合材料的组织和力学性能,并探讨了复合材料的强韧化机制.结果表明:CNTs能细化基体合金的晶粒尺寸,改变晶粒形貌及第二相的分布特征;随着CNTs添加量增大,复合材料的室温强度、断口伸长率和硬度均呈先增大后减小的趋势;当CNTs的质量分数为0.5%时,室温强度、断后伸长率和硬度最高,分别为212.2 MPa,21.1%和55.0 HBW,较基体合金的分别增加了8.5%,37.5%和10%;复合材料的强韧化机制包括增强相强化、第二相强化和细晶强化,而晶粒细化、CNTs 的润滑作用及对裂纹的阻碍作用是复合材料塑性提高的主要原因.

The carbon nanotubes (CNTs)reinforced magnesium matrix composites were fabricated by adding 0-1.5wt% CNTs into the molten Mg-1.3Mn-1.0Ce-4.0Zn alloy using stirring casting process.Microstructure and mechanical properties of the composites were studied and toughening mechanism of the composites was also discussed.The results show that grain size of the substrate alloy was refined by CNTs.Meanwhile,the grain morphology and distribution characteristics of second phase also were changed by CNTs.With the increase of CNTs′adding contents,the room temperature strength,fracture elongation and hardness all increased firstly and then decreased.When the mass fraction of CNTs was 0.5%,the composites exhibited the highest tensile strength, fracture elongation and Brinell hardness,they were 212.2 MPa,21.1% and 55.0 HBW,respectively,they respectively increased 8.5%,37.5%,10% comparing with the matrix alloy.The strengthening mechanism of the composites was reinforcement phase strengthening, second phase strengthening and fine-grain strengthening. Meanwhile,grain refinement,CNTs lubrication and CNTs retarding crack extension were mainly contributed to the improvement on plasticity.

参考文献

[1] 周天承;冯光峰.复合添加稀土钕和铒的AZ91D镁合金显微组织与拉伸性能[J].机械工程材料,2014(12):25-28,32.
[2] 翟春泉;曾小勤;丁文江;王渠东;吕宜振;徐小平.镁合金的开发与应用[J].机械工程材料,2001(1):6-10.
[3] M. Paramsothy;X.H. Tan;J. Chan;R. Kwok;M. Gupta.Carbon nanotube addition to concentrated magnesium alloy AZ81: Enhanced ductility with occasional significant increase in strength[J].Materials & design,2013Mar.(Mar.):15-23.
[4] C.D. Li;X.J. Wang;W.Q. Liu;H.L. Shi;C. Ding;X.S. Hu;M.Y. Zheng;K.Wu.Effect of solidification on microstructures and mechanical properties of carbon nanotubes reinforced magnesium matrix composite[J].Materials & design,2014Jun.(Jun.):204-208.
[5] Zeng, X.;Zhou, G.;Xu, Q.;Xiong, Y.;Luo, C.;Wu, J..A new technique for dispersion of carbon nanotube in a metal melt[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201020(20):5335-5340.
[6] M. Qian;C.S. Goh;Y.H. Sun.Effects of CNTs on microstructure and hardness of laser welds of the CNT-reinforced magnesium composite[J].Composites, Part A. Applied science and manufacturing,2013:67-72.
[7] Uozumi, H;Kobayashi, K;Nakanishi, K;Matsunaga, T;Shinozaki, K;Sakamoto, H;Tsukada, T;Masuda, C;Yoshida, M.Fabrication process of carbon nanotube/light metal matrix composites by squeeze casting[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,20081/2(1/2):282-287.
[8] Kondoh, K.;Fukuda, H.;Umeda, J.;Imai, H.;Fugetsu, B.;Endo, M..Microstructural and mechanical analysis of carbon nanotube reinforced magnesium alloy powder composites[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,201016/17(16/17):4103-4108.
[9] Y. Shimizu;S. Miki;T. Soga.Multi-walled carbon nanotube-reinforced magnesium alloy composites[J].Scripta materialia,20084(4):267-270.
[10] 刘灵 .合金化与形变热处理对Mg-Mn-Ce合金组织与性能的影响[D].湖南大学,2013.
[11] 周国华 .碳纳米管/AZ31镁基复合材料的制备与等径角挤压研究[D].南昌大学,2010.
[12] 周国华;曾效舒;张湛;罗超.碳纳米管对AZ31镁合金抗腐蚀性能影响与机制研究[J].稀有金属材料与工程,2011(1):101-105.
[13] 郭鲤;蔡晓兰;周蕾;易峰;李铮.碳纳米管增强铝基复合材料的研究进展[J].机械工程材料,2014(9):1-5,11.
[14] 杨益 .碳纳米管增强镁基复合材料的制备与性能研究[D].国防科学技术大学,2006.
[15] S.F. Hassan;M. Gupta.Effect of particulate size of Al_2O_3 reinforcement on microstructure and mechanical behavior of solidification processed elemental Mg[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20061/2(1/2):84-90.
[16] S.F. Hassan;M. Gupta.Development of nano-Y_2O_3 containing magnesium nanocomposites using solidification processing[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20071/2(1/2):176-183.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%